Abstract:<section class="article-section__content"><h3 class="article-section__sub-title section1"> BACKGROUND</h3><p>Selective catalytic reduction (SCR) of NO<sub>X</sub> has been the most widely used technique for the reduction of NO<sub>X</sub> emissions from combustion flue gas. MnO<sub>X</sub>/FeO<sub>X</sub> based catalysts typically can attain high NO<sub>X</sub> conversion at low temperature but inferior water vapor resistance. </p></section><section class="article-section__content"><h3 class="article-section__sub-title section1"> RESULTS</h3><p>A MnO<sub>X</sub>/FeO<sub>X</sub> catalyst was synthesized by the sonicated co‐precipitation method and then wash‐coated on ceramic cordierite monoliths to form a low pressure drop monolithic catalyst suitable for high flowrate flue gas treatment conditions. The catalyst achieved above 90% NO conversion at a gas hourly space velocity (GHSV) of 30,000 h<sup>‐1</sup> over a 125‐225 °C temperature window under simulated industrial flue gas conditions. In the presence of up to 5% H<sub>2</sub>O vapor, comparable performance was retained for a reduced temperature window of ≥150 °C. In order to improve water resistance and LT‐SCR performance, an optimal 10% w/w PTFE doped MnO<sub>X</sub>/FeO<sub>X</sub> catalyst was developed, which exhibited remarkably high performance of up to 98% NO conversion, with improved water resistance at up to 10% v/v H<sub>2</sub>O while retaining high performance from 100 °C. </p></section><section class="article-section__content"><h3 class="article-section__sub-title section1"> CONCLUSION</h3><p>Monolithic MnO<sub>X</sub>/FeO<sub>X</sub> catalyst incorporating PTFE significantly improved NO conversion and water vapour resistance due to the enhanced NH<sub>3</sub> adsorption associated with Lewis acid sites and water repellent property. These findings will provide guidance for researchers in this field to adapt F based or similar additives into the making of high performance and high water resistance catalysts either to retrofit existing catalyst synthesis procedures or reinvent a novel catalyst at scalable but economical way. </p><p>This article is protected by copyright. All rights reserved.</p></section>

Removal of NOx using novel Fe-Mn-Ti compound catalysts at low temperature

Catalytic performance of MnO 2-CeO 2/Ti 0.25Zr 0.25Al 0.5O 1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH 3

Highly Efficient Fe-Cu/CL Catalysts Based on Low-Cost Clay Minerals for NH3-SCR of NOx at Low Temperature

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Activation of Fast Selective Catalytic Reduction of NO by NH3 at Low Temperature over TiO2 Modified CuOX-CeOX Composites

Insights over Titanium Modified FeMgOx Catalysts for Selective Catalytic Reduction of NOx with NH3: Influence of Precursors and Crystalline Structures

Highly Dispersed Surface Active Species of Mn/Ce/TiW Catalysts for High Performance at Low Temperature NH3-SCR

Titania-Samarium-Manganese Composite Oxide for the Low-Temperature Selective Catalytic Reduction of NO with NH3

Optimization of Robust FeMnSmO x Catalyst for Low-Temperature (<150 °C) NH 3 –SCR of NO x

Synthesis and characterisation of monolithic PTFE ‐modified MnO X / FeO X catalysts for selective catalytic reduction ( SCR ) of NO X at low temperature

Low-temperature SCR of NO with NH3 over AC/C Supported Manganese-Based Monolithic Catalysts

Low Temperature Selective Catalytic Reduction of NO over Manganese Supported on TiO2 Nanotubes

Promoting Effect of Ti Species in MnOx-FeOx/Silicalite-1 for the Low-Temperature NH3-SCR Reaction

Study on the Effect of Fe Doping on SCR Activity and Reaction Mechanism of Mn–TiO2 Catalysts

Low Temperature Selective Catalytic Reduction Of No With Nh3 Over Mn-Fe Spinel: Performance, Mechanism And Kinetic Study

Transition metals (Co, Zr, Ti) modified iron-samarium oxide as efficient catalysts for selective catalytic reduction of NOx at low-temperature

Fe and Mn mixed oxide catalysts supported on Sn-modified TiO 2 for the selective catalytic reduction of NO with NH 3 at low temperature

Effect of transition metals addition on the catalyst of manganese/titania for low-temperature selective catalytic reduction of nitric oxide with ammonia

Improvement of sulfur and water resistance with Fe-modified S-MnCoCe/Ti/Si catalyst for low-temperature selective catalytic reduction of NO with NH3

Selective Catalytic Reduction of NO by NH3 on Fe, Mn-based Catalysts