Abstract:The selective catalytic reduction (SCR) technique that converts NOx from the outlet of industrial boilers at low temperature (<200 °C) requires catalysts that possess both the oxidization property of NOx and the adsorption ability to NH3. However, owing to unsuitable redox capacity, most NH3-SCR catalysts such as MnO2/TiO2 and MnO2–CeO2/TiO2 suffer from poor activity and N2 selectivity and SO2 poisoning. Benefiting from constructing mesoporous MnCeSmTiOx amorphous mixed oxides by the coprecipitation method, enhanced SO2-tolerant low-temperature NH3-SCR performance was achieved. The MnCeSmTiOx catalysts have an amorphous and mesoporous structure with a BET surface area of 214 m2·g–1. The NO conversion could reach nearly 100% at 140–320 °C and maintain >90% at 400 °C and a gas hourly space velocity of 80,000 h–1. The selectivity of N2 could be maintained at ≈100% at 100–320 °C and stay at >90% up to 400 °C. Besides, the MnCeSmTiOx catalyst preserves higher catalytic performance after introducing H2O and SO2 compared with the catalysts without adding Sm. The redox properties, acidic properties, and reaction intermediates of catalysts were analyzed by X-ray photoelectron spectroscopy, hydrogen temperature-programmed reduction, ammonia temperature-programmed desorption (NH3-TPD), O2-TPD, pyridine-IR, thermogravimetry–differential scanning calorimetry, and diffuse reflectance infrared Fourier transform. The synergistic effect of the Lewis acid sites and oxidation catalytic sites of mixed oxides serves for the conversion of NO to N2 by following the Langmuir–Hinshelwood mechanism. Doping Sm into MnCeSmTiOx can increase oxygen vacancies and transfer electrons to Mn4+ and Ce4+, which facilities the formation of active adsorbed NO2, bidentate nitrate, and bridging nitrate intermediates and suppresses SO2 poisoning by inhibiting the oxidation of SO2 by Mn4+ and Ce4+. Our work could be beneficial to modulate the redox capacity of active sites on NH3-SCR catalysts so that NOx can be eliminated in complex flue gas at low temperatures.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c02567?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c02567</a>.Experimental details, kinetic experiments and the calculation process of the reaction rate, reaction order, and TOF; XRD patterns; TEM images; and in situ DRIFTS spectra with adsorption of NH3 NO + O2 on MnSmTiOx and CeSmTiOx catalysts (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c02567/suppl_file/cs0c02567_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Synthesis and characterisation of monolithic PTFE ‐modified MnO X / FeO X catalysts for selective catalytic reduction ( SCR ) of NO X at low temperature

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

Low-temperature SCR of NO with NH3 over AC/C Supported Manganese-Based Monolithic Catalysts

Improved Activity and SO 2 Resistance by Sm-Modulated Redox of MnCeSmTiO x Mesoporous Amorphous Oxides for Low-Temperature NH 3 -SCR of NO

Ultralow-Temperature NOx Reduction over SmMn2O5 Mullite Catalysts Via Modulating the Superficial Dual-Functional Active Sites

Low Temperature Selective Catalytic Reduction Of No With Nh3 Over Mn-Fe Spinel: Performance, Mechanism And Kinetic Study

Titania-Samarium-Manganese Composite Oxide for the Low-Temperature Selective Catalytic Reduction of NO with NH3

Low-temperature SCR of NOx by NH3 over MnOx/SAPO-34 prepared by two different methods: a comparative study

Optimization of Robust FeMnSmO x Catalyst for Low-Temperature (<150 °C) NH 3 –SCR of NO x

Bimetallic modification of MnFeO nanobelts with Nb and Nd for enhanced low-temperature de-NO performance and SO2 tolerance

Improvement of sulfur and water resistance with Fe-modified S-MnCoCe/Ti/Si catalyst for low-temperature selective catalytic reduction of NO with NH3

Selective catalytic reduction of NOx with NH3 by monolithic catalyst MnOx/AC/C under low temperature in the presence of excess O2

Flexible monolithic Pt/CuO-Fe2O3/TiO2 catalysts integrated on Ti mesh for efficient NO removal via CO-SCR reaction

Effect of Preferential Exposure of Anatase TiO2 {0 0 1} Facets on the Performance of Mn-Ce/TiO2 Catalysts for Low-Temperature Selective Catalytic Reduction of NOx with NH3

A novel high activity MnXFe3−XO4 spinel catalyst for selective catalytic reduction of NO using NH3 prepared by a short process from natural minerals for low-temperature sintering flue gas: Effect of X value on catalytic mechanism

High Resistance of SO2 and H2O over Monolithic Mn-Fe-Ce-Al-O Catalyst for Low Temperature NH3-SCR

The development of Fe2O3-based catalysts used for the selective catalytic reduction of NO with NH3: A review

Highly efficient MnCe/Ti catalyst for NH 3 -SCR of NO from sintering flue gas at low temperature: CO tolerance and reaction mechanism assessed by in situ DRIFTS

Advanced Mnox/Tio2 Catalyst with Preferentially Exposed Anatase {001} Facet for Low-Temperature Scr of No

Low Temperature Selective Catalytic Reduction of NO over Manganese Supported on TiO2 Nanotubes