Abstract:A series of Fe-Mn/Al2O3 catalysts were prepared and studied for low temperature selective catalytic reduction (SCR) of NO with NH3 in a fixed-bed reactor. The effects of Fe and Mn on NO conversion and the deactivation of the catalysts were studied. N2 adsorption-desorption, X-ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, H2 temperature-programmed reduction, NH3 temperature-programmed desorption, X-ray photoelectron spectroscopy (XPS), thermal gravimetric analysis and Fourier transform infrared spectroscopy were used to characterize the catalysts. The 8Fe-8Mn/Al2O3 catalyst gave 99% of NO conversion at 150 °C and more than 92.6% NO conversion was obtained in a wide low temperature range of 90–210 °C. XPS analysis demonstrated that the Fe3+ was the main iron valence state on the catalyst surface and the addition of Mn increased the accumulation of Fe on the surface. The higher specific surface area, enhanced dispersion of amorphous Fe and Mn, improved reduction properties and surface acidity, lower binding energy, higher Mn4+/Mn3+ ratio and more adsorbed oxygen species resulted in higher NO conversion for the 8Fe-8Mn/Al2O3 catalyst. In addition, the SCR activity of the 8Fe-8Mn/Al2O3 catalyst was only slightly decreased in the presence of H2O and SO2, which indicated that the catalyst had better tolerance to H2O and SO2. The reaction temperature was crucial for the SO2 resistance of catalyst and the decrease of catalytic activity caused by SO2 was mainly due to the sulfate salts formed on the catalyst.

Low-temperature SCR of NOx by NH3 over MnOx/SAPO-34 prepared by two different methods: a comparative study

In Situ FT-IR Study of Highly Dispersed MnO X /SAPO-34 Catalyst for Low-Temperature Selective Catalytic Reduction of NO X by NH 3

MnO<sub>x</sub> Supported on Hierarchical SAPO-34 for the Low-Temperature Selective Catalytic Reduction of NO with NH<sub>3</sub>: Catalytic Activity and SO<sub>2</sub> Resistance

Mn/SAPO-34 As an Efficient Catalyst for the Low-Temperature Selective Catalytic Reduction of NOx with NH3

an e ffi cient catalyst for the low-temperature selective catalytic reduction of NO x with NH 3

Sulfur and Water Resistance of Mn-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NOx: A Review

Low Temperature Selective Catalytic Reduction of NOx with NH3 over Amorphous MnOx Catalysts Prepared by Three Methods

Abundant Oxygen Vacancies Induced by the Mechanochemical Process Boost the Low-Temperature Catalytic Performance of MnO2 in NH3-SCR

Low-temperature SCR of NO with NH3 over AC/C Supported Manganese-Based Monolithic Catalysts

Manganese-rich MnSAPO-34 molecular sieves as an efficient catalyst for the selective catalytic reduction of NO x with NH 3 : one-pot synthesis, catalytic performance, and characterization

Performance of Low-temperature SCR of NO with NH3 over MnOx/Ti-based catalysts

Ni-Mn Bi-Metal Oxide Catalysts for the Low Temperature SCR Removal of NO with NH3

Low-cost Mn-Fe/SAPO-34 catalyst from natural ferromanganese ore and lithium-silicon-powder waste for efficient low-temperature NH3-SCR removal of NOx

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Novel Mn–Zr Mixed Oxide Catalysts

Structures and catalytic performances of Me/SAPO-34 (Me = Mn, Ni, Co) catalysts for low-tem perature SCR of NO by ammonia

A One-Pot Synthesis of Cu-modified Mn-rich MnSAPO-34 Catalyst with Excellent Low Temperature NH3-selective Catalytic Reduction Performance and H2O Resistance

Structures and Catalytic Performances of Me/SAPO-34(Me=Mn,Ni,Co) Catalysts for Low-Tem Perature SCR of NO X by Ammonia

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

Promoting Effect of Si on MnOx Catalysts for Low-Temperature NH3-SCR of NO: Enhanced N2 Selectivity and SO2 Resistance

SO2 Deactivation Mechanism of MnOx/MWCNTs Catalyst for Low-Temperature Selective Catalytic Reduction of NOx by Ammonia

Porous MnOx for Low-Temperature NH3-SCR of NOx: the Intrinsic Relationship Between Surface Physicochemical Property and Catalytic Activity