Abstract:A series of TiO2-M(M = Sn, Zr or Al) O-x were prepared and manganese oxide (MnOx) was supported on the carrier by the traditional impregnation method for low-temperature selective catalytic reduction (SCR) of NOx with ammonia as a reductant. The obtained catalysts were characterized by XRD, BET, high-resolution transmission electron microscope (HRTEM), H-2-TPR, NH3-TPD, X-ray photoelectron spectroscopy (XPS) and in situ Fourier-transform infrared (FT-IR) and their catalytic activities for NOx reduction with NH3 in the presence of SO2 were investigated comparatively. The results showed that the highest NOx conversion of over 90% could be obtained with the Mn/Ti-Sn catalyst at a wide range of temperature window of 150-270 degrees C. The combination of characterization techniques, such as BET, XRD and HRTEM, revealed that manganese oxides were well dispersed on Ti-Sn. H-2-TPR suggested that Ti-Sn and Ti-Zr supports could enhance the reduction ability of catalysts. Accordingly, Mn/Ti-Al exhibited worse activity at low temperature. XPS results were in good agreement with H-2-TPR results, and Mn/Ti-Sn had more surface-reducible species of Mn4+ ions and more surface-adsorbed oxygen species, which was conducive to SCR reaction. The in situ FT-IR spectra of NH3 adsorption indicated that all the modified catalysts had more Lewis acid sites and the amide species at 1506cm(-1) had a certain influence on the catalytic reaction at low temperature. Mn/Ti-Zr showed a stronger resistance to SO2 but Mn/Ti-Al was affected more adversely and all the catalysts could not be restored to the initial catalytic activity after stopping feeding SO2. NH3-TPD revealed that the total acid amount of the Mn/Ti-Sn sample was larger than other samples, which indicated that the Ti-Sn solid solution could provide more surface acid sites over the catalyst.

Effect of transition metals addition on the catalyst of manganese/titania for low-temperature selective catalytic reduction of nitric oxide with ammonia

Influence of the Addition of Transition Metals (cr, Zr, Mo) on the Properties of MnO X –feo X Catalysts for Low-Temperature Selective Catalytic Reduction of NO X by Ammonia

Enhancement of Low-Temperature Catalytic Activity over a Highly Dispersed Fe–Mn/Ti Catalyst for Selective Catalytic Reduction of NOx with NH3

Effects of ferric and manganese precursors on catalytic activity of Fe-Mn/TiO2 catalysts for selective reduction of NO with ammonia at low temperature

Study on the Effect of Fe Doping on SCR Activity and Reaction Mechanism of Mn–TiO2 Catalysts

Influence of WO3 doping on properties of MnOx/TiO2 catalyst for low-temperature selective catalytic reduction of NOx by NH3

Insights into the Highly Efficient Co Modified MnSm/Ti Catalyst for Selective Catalytic Reduction of NOx with NH3 at Low Temperature

Low-Temperature Selective Catalytic Reduction of NO with NH3 Over Mn–Ti Oxide Catalyst: Effect of the Synthesis Conditions

Transition metals (Co, Zr, Ti) modified iron-samarium oxide as efficient catalysts for selective catalytic reduction of NOx at low-temperature

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Fe–Mn Mixed-Oxide Catalysts Containing Fe3Mn3O8 Phase

Ni-Mn Bi-Metal Oxide Catalysts for the Low Temperature SCR Removal of NO with NH3

A Comparative Study on the Mn/TiO2-M(M = Sn, Zr or Al) Ox Catalysts for NH3-SCR Reaction at Low Temperature

The role of NH3 in the low-temperature selective catalytic reduction of NO over MnOx/TiO2

Novel Ultrasonic-Modified MnOx/TiO2 for Low-Temperature Selective Catalytic Reduction (SCR) of NO with Ammonia.

Fe–Mn Mixed Oxide Catalysts Synthesized by One-Step Urea-Precipitation Method for the Selective Catalytic Reduction of NOx with NH3 at Low Temperatures

Efficient Sm Modified Mn/TiO2 Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Catalytic performance of MnO_x/WO_3/TiO_2 catalyst for low-temperature selective catalytic reduction of NO_x by NH_3

Effect of Fe on the Selective Catalytic Reduction of NO by NH3 at Low Temperature over Mn/CeO2-TiO2 Catalyst

Transition Metal Doped MnOx-CeO2 Catalysts by Ultrasonic Immersing for Selective Catalytic Reduction of NO with NH3 at Low Temperature

DRIFT Study of Manganese/Titania-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NO with NH<sub>3</sub>