Abstract:Non-uniform corrosion of steel reinforcing bars is the main cause of structural failure in civil engineering. However, the accurate measurement of the critically corroded cross-sectional area, or the pit shape, is difficult owing to conventional limitations on detection. To accurately represent the corrosion morphology and better understand the corrosion effects on the tensile responses of deformed steel bars, a three-dimensional model of a corroded steel bar was reconstructed using a three-dimensional (3D) laser scanner. Based on the elicited 3D profiles, the corrosion factors-including the corrosion uniformity-the average, and maximum cross-sectional areas and their relationships, were identified in this study. The statistical analyses indicated that the number of corroded pits and their depths increased when the corrosion rate increased, and that decreases of the critical cross-sectional areas were linearly related to the average mass loss. Axial tensile tests of corroded steel bars were also carried out. The tensile test results showed that both the yield and the ultimate loads linearly decreased with increases in corrosion loss. Corresponding decreases in ductility were also observed. Compared with the degradation in the strength, the non-uniform corrosion had a considerable effect on the loss of ductility. The relationships between the mechanical parameters and the corrosion factors were established on the basis of the experimental results, and compared with the available prediction models. It was found that fractures originated at the locations of the critically corroded pit, and brittle fracture gradually occurred at the weakest location of the corroded steel bar, evidenced by concomitant increases in corrosion loss. Numerical simulations were carried out to clarify the critical section, the effect of pit corrosion on the concentration of stress, and the tensile response of the corroded steel bar, based on the 3D model reconstructed using scanning.

Multifractal Analysis of Reinforcing Steel Bars with Nonuniform Corrosion Degree

Comparing Monofractal And Multifractal Analysis Of Corrosion Damage Evolution In Reinforcing Bars

Ultra-low Cycle Fatigue Properties and Fracture Mechanism of Corroded Structural Steel

Fractal Characterization of Non-Uniform Corrosion of Steel Bars in Concrete Beams after Accelerated Depassivation and Seven-Year Natural Corrosion.

Fractal characterization of corroded surface profile in reinforcing steel bars

Probability-Based Performance Degradation Model and Constitutive Model for the Buckling Behavior of Corroded Steel Bars

Effect Of Corroded Surface Morphology On Ultra-Low Cycle Fatigue Of Steel Bridge Piers

Evaluation of corrosion morphology on mechanical properties of reinforcing steel bars using numerical simulation and simplified analytical model

Fractal Based Characterization of Nonuniform Corroded Surface Profile in Steel Bars

Fractal Characteristics of Corrosion-Induced Cracks in Reinforced Concrete.

Influence of Coupled Chemo-Mechanical Process on Corrosion Characteristics in Reinforcing Bars

Non-Uniform Distribution of A Corrosion Layer at A Steel/Concrete Interface Described by A Gaussian Model

Stochastic Characteristics of Reinforcement Corrosion in Concrete Beams under Sustained Loads

Measurement pitting morphology characteristic of corroded steel surface and fractal reconstruction model

Study on Experimental Method and Morphology of Accelerated Non-Uniform Corrosion of Steel Bars

Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion

Fracture Behavior of Mild Steel Based on Numerical Algorithm

Evaluation of Corrosion Characteristics and Corrosion Effects on the Mechanical Properties of Reinforcing Steel Bars Based on Three-Dimensional Scanning

Non-uniform distribution of rust layer around steel bar in concrete

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

Prediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures