Abstract:In this study, a new casing process named expendable pattern shell casting process with vacuum and low pressure (EPSC-VL) was introduced to produce complicated and thin-walled aluminum alloy castings. The gas flowrate is one of the most important process parameters for manufacturing castings during the EPSC-VL process. In the present work, the influence of gas flowrate on the filling ability and internal quality of A356 aluminum alloy castings fabricated by the EPSC-VL process were investigated. Moreover, the filling ability, internal quality, as well as mechanical properties of A356 aluminum alloy castings obtained by EPSC-VL and lost foam casting (LFC) processes were also compared. The results obtained suggested that the filling length increased with the increase of gas flowrate, and the filling length of the thick section was larger than that of the thin section under the same gas flowrate when the gas flowrate was less than 19 m(3)/h. Furthermore, the porosity of castings decreased with increasing gas flowrate, and the microstructure of castings became denser, and the internal quality of castings was obviously improved. The comparison experiments showed that the EPSC-VL process had superior filling ability, internal quality, and mechanical properties compared with the LFC process, and the surface quality of castings obtained by EPSC-VL process was also better than that of the LFC process. The casting practice of complicated and thin-walled A356 aluminum alloy intake manifold part also suggested that the EPSC-VL process had an obvious advantage for the fabrication of complicated and thin-walled aluminum alloy castings compared with the LFC process.

Processing Parameters of LFC Shell Mold Casting Aluminum Alloy Castings with Vacuum and Low Pressure

Influence of Process Parameters on Filling Ability of A356 Aluminium Alloy in Expendable Pattern Shell Casting with Vacuum and Low Pressure

Effects of Process Parameters on Internal Quality of Castings During Novel Casting

Influence of Gas Flowrate on Filling Ability and Internal Quality of A356 Aluminum Alloy Castings Fabricated Using the Expendable Pattern Shell Casting with Vacuum and Low Pressure

Process Optimization of Low-pressure Die Casting of Aluminum Alloy Wheel based on Taguchi Method

Prediction method of shrinkage cavity and shrinkage porosity in solidification process under low-pressure casting

Investigation of Microstructures and Mechanical Properties of A356 Aluminum Alloy Produced by Expendable Pattern Shell Casting Process with Vacuum and Low Pressure

Characteristics of Mold Filling and Entrainment of Oxide Film in Low Pressure Casting of A356 Alloy

Determination of Optimal Temperature for Defect-Free Casting of Aluminium in the LP-LFC Process

Study of fabricating technology of a porous aluminum alloy

Determination of casting parameters of thick wall die-casting of magnesium alloy and simulation of its processing

Study on vacuum die casting process of aluminum alloys

Optimization of low-pressure die casting process parameters for reduction of shrinkage porosity in ZL205A alloy casting using Taguchi method

Low-pressure die casting of magnesium alloy AM50: Response to process parameters

Mold filling velocity during investment casting

Effects of Hollow Sand Mold on the Microstructure and Mechanical Properties of a Low Pressure Aluminum Alloy Casting

Effects of Vacuum Die Casting Processing Parameters on Mechanical Properties of AM50 Magnesium Alloy

Effect of Vacuum Degree on Quality of Magnesium Alloy by Low-Pressure Expendable Pattern Casting

Low pressure casting technology and forming process analysis of metal mold based on ProCAST FEA procedure

Analysis of Formation Mechanism of Typical Defects in Aluminum (Magnesium) Alloys Castings by the Expendable Pattern Shell Casting with Vacuum and Low Pressure

Key Analysis of Design and Numerical Simulation for Aluminum Alloy Impeller Low-pressure Casting Mold