Abstract:ZL205A alloys are prone to generate serious residual stress due to the long solidification intervals and multiphase composition. In this study, the low-pressure casting process for ZL205A alloy hemisphere shell casting was investigated and continuously optimized. In the initial process, the knockout time, pouring temperature, preheating temperature of the sand mould, dwelling pressure, and filling rate were 3 h, 710 degrees C, 30 degrees C, 65 kPa, and 0.33 kPa center dot s(-1), respectively. Macroscopic properties and microstructural features were simulated using a combination of ProCAST and Thermal-Calc software. Additionally, a series of experimental procedures, including EBSD, SEM, EDS, and XRD tests, were conducted to investigate the formation, morphology, and distribution of the microstructure. Current findings demonstrate that during the solidification process, the maximum temperature difference exceeds 220 degrees C, the maximum undercooling reaches 49.56. degrees C, and the maximum effective stress peaks at 301.7 MPa. The residual stress ranges from 20 to 200 MPa. Furthermore, there is no significant texture and preferred grain orientation during nucleation and solidification, and the structure field exhibits an equiaxed crystal but inhomogeneous pattern. Moreover, the finer and more homogeneous the grains and the smaller the deviation in grain orientation, the lower the residual stress. Specifically, two analytical models are developed: one between the casting parameters and the residual stress, and another between the shrinkage defects and the casting parameters. The lowest residual stress is achieved when the knockout time, pouring temperature, pre-heating temperature of the sand mould, dwelling pressure, and filling rate are 6 h, 725 degrees C, 250 degrees C, 95 kPa, and 1.67 kPa center dot s(-1) respectively.

Determination of Optimal Temperature for Defect-Free Casting of Aluminium in the LP-LFC Process

Porosity of aluminum alloy in lost foam casting process

Process Optimization of Low-pressure Die Casting of Aluminum Alloy Wheel based on Taguchi Method

Study on the Cavity Defects of Low-Pressure Lost Foam Casting for Magnesium Alloy

Investigation on the Mechanism of the Pinhole Formation of Aluminum Alloy LFC Process

Determination of casting parameters of thick wall die-casting of magnesium alloy and simulation of its processing

Study on Typical Hole Defects in Az91d Magnesium Alloy Prepared by Low Pressure Lost Foam Casting

Processing Parameters of LFC Shell Mold Casting Aluminum Alloy Castings with Vacuum and Low Pressure

Optimization of residual stress in low-pressure casting of ZL205A alloys

Study on Structure and Corrosion Resistance of AZ91 Magnesium Alloy in Lost Foam Casting Process

Influence of Laser-Based Powder Bed Fusion of Metals Process Parameters on the Formation of Defects in Al-Zn-Mg-Cu Alloy Using Path Analysis

Low-pressure die casting of magnesium alloy AM50: Response to process parameters

Fluidity of AZ91D and Mg–3Nd–0·2Zn–Zr (Wt-%) Magnesium Alloys: Response to Pouring and Mould Temperature

Optimization and Design Based On Numerical Simulation of AZ91D Die Casting Gating and Runner System

Effects of cooling rates on microporosity in DC casting Al-Li alloy

Mass Transfer of Lost Foam Casting and Its Influence on the Casting Quality

Effects of Process Parameters on Internal Quality of Castings During Novel Casting

Effect of Cooling Process on Porosity in the Aluminum Alloy Automotive Wheel During Low-Pressure Die Casting

Numerical Simulation of Lost-Foam Casting for Key Components of A356 Aluminum Alloy in New Energy Vehicles

A New Way to Cast High-Alloyed Al–Zn–Mg–Cu–Zr for Super-High Strength and Toughness

Experiment and Numerical Simulation of Microstructure of ZL114A Alloy in Low Pressure Casting