Abstract:The Ti-6Al-4V (TC4) alloy wheel hub has exhibited some defects that affect the properties during the vertical centrifugal casting process. Therefore, the analysis of the solidification process would contribute to solving the above-mentioned problems. In this study, an orthogonal experimental design was employed to optimize the process parameters (rotational speed, mold preheating temperature, and pouring temperature) of the vertical centrifugal casting method. The effects of process parameters on the velocity field, temperature field, and total shrinkage porosity during the solidification process were explored, and the microstructure and mechanical properties of the wheel hub prepared by the vertical centrifugal casting method were also investigated. The results showed that the rotational speed mainly induced the change of the velocity field. The pouring temperature and mold preheating temperature affected the temperature field and solidification time. Based on the analysis of the orthogonal experiment, the optimal parameters were confirmed as a rotational speed of 225 rpm, mold preheating temperature of 400 °C, and pouring temperature of 1750 °C, respectively. The simulation results of total shrinkage porosity were in agreement with the experiment results. The wheel hub was composed of nonuniform α and β phases. The lath α phase precipitated from larger β grains with different orientations. Compared with the other samples at different locations, the α phase in the PM sample (middle of the TC4 wheel hub) displayed high peak intensity and uniformly distributed β phase along the radial direction of the wheel hub. Moreover, the PM sample revealed a higher tensile strength of 820 MPa and similar Vickers hardness of 318 HV compared with the other samples at different locations, which were higher than those of rolling and extrusion molding. This experiment design would provide a good reference for the vertical centrifugal casting of the TC4 alloy.

Process Optimization of Low-pressure Die Casting of Aluminum Alloy Wheel based on Taguchi Method

Die Structure Optimization of Aluminum Alloy Wheel Low-Pressure Die Casting Based on CAE

Study on Simulation of Stamping Forming and Die Surface Optimization of Aluminum Alloy Plate

Optimization of Low-Pressure Die Casting Process with Soft Computing

Multi-Objective Optimization of The Low-Pressure Casting of Large-Size Aluminum Alloy Wheels through a Systematic Optimization Idea

Optimization of low-pressure die casting process parameters for reduction of shrinkage porosity in ZL205A alloy casting using Taguchi method

Study of Mold Filling Simulation on Low Pressure Die Casting for Automobile Wheel Casting

Optimization of Valve Body Process Based on HZCAE

Prediction method of shrinkage cavity and shrinkage porosity in solidification process under low-pressure casting

Prediction of Fatigue Life for Automotive A-Alloy Wheel with Integrated Cast Defects

Determination of casting parameters of thick wall die-casting of magnesium alloy and simulation of its processing

Mold Local Temperature Control in Low Pressure Die Casting Aluminum Alloy Wheel Hub

Numerical Simulation of Filling Process and Technology Improvement of Low Pressure Die Casting of Aluminum Wheel Hub

Solidification simulation of automobile wheel in low pressure casting

Die casting process optimization using Taguchi methods

Optimization of Casting System Structure Based on Genetic Algorithm for A356 Casting Quality Prediction

Optimization of Die casting process based on Taguchi approach

Numerical Simulation and Optimization of Indirect Squeeze Casting Process

Simulation of Casting Stress of Low-pressure Casting Aluminum Alloy Wheel

Numerical Simulation on Solidification during Vertical Centrifugal Casting Process for TC4 Alloy Wheel Hub with Enhanced Mechanical Properties

Optimization of process parameters to improve dimensional accuracy of investment casting using Taguchi approach