Abstract:ZL205A alloys are prone to generate serious residual stress due to the long solidification intervals and multiphase composition. In this study, the low-pressure casting process for ZL205A alloy hemisphere shell casting was investigated and continuously optimized. In the initial process, the knockout time, pouring temperature, preheating temperature of the sand mould, dwelling pressure, and filling rate were 3 h, 710 degrees C, 30 degrees C, 65 kPa, and 0.33 kPa center dot s(-1), respectively. Macroscopic properties and microstructural features were simulated using a combination of ProCAST and Thermal-Calc software. Additionally, a series of experimental procedures, including EBSD, SEM, EDS, and XRD tests, were conducted to investigate the formation, morphology, and distribution of the microstructure. Current findings demonstrate that during the solidification process, the maximum temperature difference exceeds 220 degrees C, the maximum undercooling reaches 49.56. degrees C, and the maximum effective stress peaks at 301.7 MPa. The residual stress ranges from 20 to 200 MPa. Furthermore, there is no significant texture and preferred grain orientation during nucleation and solidification, and the structure field exhibits an equiaxed crystal but inhomogeneous pattern. Moreover, the finer and more homogeneous the grains and the smaller the deviation in grain orientation, the lower the residual stress. Specifically, two analytical models are developed: one between the casting parameters and the residual stress, and another between the shrinkage defects and the casting parameters. The lowest residual stress is achieved when the knockout time, pouring temperature, pre-heating temperature of the sand mould, dwelling pressure, and filling rate are 6 h, 725 degrees C, 250 degrees C, 95 kPa, and 1.67 kPa center dot s(-1) respectively.

Optimization of low-pressure die casting process parameters for reduction of shrinkage porosity in ZL205A alloy casting using Taguchi method

Process Optimization of Low-pressure Die Casting of Aluminum Alloy Wheel based on Taguchi Method

Die Structure Optimization of Aluminum Alloy Wheel Low-Pressure Die Casting Based on CAE

Prediction method of shrinkage cavity and shrinkage porosity in solidification process under low-pressure casting

Optimization of Valve Body Process Based on HZCAE

Optimization of residual stress in low-pressure casting of ZL205A alloys

Optimization of Casting System Structure Based on Genetic Algorithm for A356 Casting Quality Prediction

Determination of casting parameters of thick wall die-casting of magnesium alloy and simulation of its processing

Effects of Process Parameters on Shrinkage Porosity in 357 Semi-Solid Die Casting Parts

Optimization of Low-Pressure Die Casting Process with Soft Computing

Numerical Simulation and Optimization of Investment Casting for Complex Thin-walled Castings

Optimization of process parameters to improve dimensional accuracy of investment casting using Taguchi approach

Optimization of investment casting process for K477 superalloy aero-engine turbine nozzle by simulation and experiment

Optimization of squeeze casting process of gearbox cover based on FEM and Box-Behnken design

Studies on formation of shrinkage cavity and porosity of steel castings by taking filling process into account

Continuous Casting Mould for Square Steel Billet Optimised by Solidification Shrinkage Simulation

Optimization of vacuum counter-pressure casting process for an aluminum alloy casing using numerical simulation and defect recognition techniques

Numerical simulation of shrinkage porosity defect in billet continuous casting

Low pressure casting technology and forming process analysis of metal mold based on ProCAST FEA procedure

Microstructure phase analysis and process optimization of ZL205A metal mold casting

High-pressure die casting process optimization for improving shrinkage porosity and air entrainment in carburetor housing with aluminum alloy using Taguchi-based ProCAST simulation and MADM-based overall quality index