Abstract:The hole defects can easily occur in magnesium alloy castings that are prepared by low pressure lost foam casting (LP-LFC) process when the process parameters such as vacuum, pouring temperature and filling velocity are not properly selected. In this study, the forming mechanism of the hole defects in AZ91D magnesium castings by LP-LFC process was investigated. The shape, location and surface appearance of the hole defects were observed using optical microscopy and scanning electron microscopy, and the chemical composition on the surface of the holes was analyzed using energy spectrometer. The result indicates that there are two types of hole defects, i.e., the pyrolysis products related hole defects, including concentrative hole and blow hole defects, and slag related hole defects. The concentrative hole and the blow-hole defects were formed either by the liquid-EPS degradation products entrapped in the molten metal under the condition that the pouring temperature is equal to or lower than 730 ℃, or by the hindered transport of EPS pyrolysis products. Some irregular shape hole defects were caused by slag or by coating slough entrapment when the pouring temperature is equal to 750 ℃ and the filling velocity is equal to or greater than 100 mm·s-1. To reduce or eliminate the hole defects, the vacuum and filling velocity must be properly chosen to ensure that the metal front profile exhibits convex shape and in laminar current state, and the pouring temperature should be just high enough to ensure that the molten melt has adequate heat energy to complete the foam pyrolysis and to fully occupy the mould. For AZ91D magnesium castings in this study, the parameters should be 730 ℃ pouring temperature, 0.02-0.03 MPa vacuum and 80 mm·s-1 filling velocity.

Analysis of Formation Mechanism of Typical Defects in Aluminum (Magnesium) Alloys Castings by the Expendable Pattern Shell Casting with Vacuum and Low Pressure

Casting defects and microstructure distribution characteristics of aluminum alloy cylinder head with complex structure

Defects Analysis and Improvement for Electricmotorcar Aluminum Alloy Wheel by Gravity Casting

Study on Typical Hole Defects in Az91d Magnesium Alloy Prepared by Low Pressure Lost Foam Casting

Study on the Cavity Defects of Low-Pressure Lost Foam Casting for Magnesium Alloy

Formation Mechanism of Surface Crack in Low Pressure Casting of A360 Alloy

The molding analysis of automobile parts using the die-casting system

Investigation on Surface Defects Produced in Pretreatment of Die-casting AM60B Magnesium Alloy

Correlation of Microstructure with Mechanical Properties and Fracture Behavior of A356-T6 Aluminum Alloy Fabricated by Expendable Pattern Shell Casting with Vacuum and Low-Pressure, Gravity Casting and Lost Foam Casting

Numerical and Experimental Analysis on Runner and Gate Positioning for Magnesium Alloy Die-Casted Test Piece

Investigation of Microstructures and Mechanical Properties of A356 Aluminum Alloy Produced by Expendable Pattern Shell Casting Process with Vacuum and Low Pressure

Casting defects and fatigue strength of a die cast aluminium alloy: a comparison between standard specimens and production components

Effects of Process Parameters on Internal Quality of Castings During Novel Casting

Influence of Melt Flow on the Formation of Defect Band in High Pressure Die Casting of Az91d Magnesium Alloy

Study on the Influence of Injection Velocity on the Evolution of Hole Defects in Die-Cast Aluminum Alloy

Influence of Laser-Based Powder Bed Fusion of Metals Process Parameters on the Formation of Defects in Al-Zn-Mg-Cu Alloy Using Path Analysis

Effects of Hollow Sand Mold on the Microstructure and Mechanical Properties of a Low Pressure Aluminum Alloy Casting

Modelling Generation Mechanism of Defects During Permanent Mould Centrifugal Casting Process of TiAl Alloy Exhaust Valve

Computation Method for Mechanical Performances of Die-Cast Aluminum Alloys Based on Non-Uniform Material Properties

Effects of Runner Design and Pressurization on the Microstructure of a High-Pressure Die Cast Mg-3.0Nd-0.3Zn-0.6Zr Alloy