Influence of synthesis method and processing on the thermoelectric properties of CoSb3 skutterudites
M. Uday Kumar,R. Swetha,B. V. Sahana,Ramappa S. Kuri,Bogdan Popescu,Ilhame Assahsahi,Latha Kumari
DOI: https://doi.org/10.1007/s10854-024-12277-1
2024-03-06
Journal of Materials Science Materials in Electronics
Abstract:In the present work, single phase CoSb 3 skutterudite nanomaterials were prepared via a ball milling method, and their thermoelectric characteristics were compared with the samples synthesized by the solvo-hydrothermal method. Thermoelectric transport properties were recorded in the temperature regime of 300–830 K. Both samples exhibit p-type conduction behavior with a positive sign of Seebeck coefficient. CoSb 3 ball mill sample exhibit higher resistivity of 127 × Ω.m at 300 K as compared to CoSb 3 solvo-hydrothermal sample with 4.85 × Ω.m. However, CoSb 3 ball mill sample show enhanced Seebeck coefficient of 183μ V/K at 473 K where CoSb 3 solvo-hydrothermal sample depict 98 μ V/K at 650 K. Furthermore, the total thermal conductivity of sintered CoSb 3 ball mill and CoSb 3 solvo-hydrothermal samples was found to be 3.02 Wm −1 K −1 and 3.23 W m −1 K −1 at room temperature and reaches a significantly lower value of 2.47 W m −1 K −1 and 2.46 W m −1 K −1 at 580 and 670 K, respectively. The dimensionless figure of merit ZT values of CoSb 3 ball mill and CoSb 3 solvo-hydrothermal obtained are 0.053 and 0.060 at 650 and 700 K, respectively. A systematic tuning of processing parameters by ball milling method can lead to better thermoelectric efficiency.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied