Abstract:In this work, single-phase Te-doped CoSb 3 polycrystalline bulk (Indium powder) and nanocomposites (α-WC nanopowder) were synthesized via a ball milling, hand-grinding and consolidated by spark plasma sintering technique. The thermoelectric and mechanical characteristics of as-synthesized composites were studied. The electrical resistivity varies between 11.82 and 12.82 μΩ-m for CoSb 2.875 Te 0.125 + x ( x = 0.33% In, 1% In, 2% In, 4% In and 1% In + 0.33% α-WC, respectively) composites. At temperature of 300 K, composite with x = 1% In exhibit the lowest resistivity of 11.82 μΩ-m. Also, negative values of Seebeck coefficients confirm that electrons are the predominant charge carriers. The maximum power factor of 2566 and 2482 μWm −1 K −2 are observed from x = 1% In and x = 1% In + 0.33% α-WC composites at 673 K, respectively. Notably, the power factor of 1% In and 1% In + 0.33% α-WC composites is slightly higher (1.05 times) than the CoSb 2.875 Te 0.125 sample. The composites with lowest weight percent of 1% In and 1% In + 0.33% α-WC have a considerably improved power factor. For the composite with x = 1% In + 0.33% α-WC, the minimum thermal conductivity of 2.32 W/m–K at 300 K was achieved through a combination of doping and dispersion in the CoSb 2.875 Te 0.125 matrix. It is possible that the multi-scale size distributions of grains will reduce the lattice thermal conductivity by scattering phonons over a large wavelength range. As a result, an increased figure of merit of 0.82 was achieved for CoSb 2.875 Te 0.125 + 1% In + 0.33% α-WC composites at 823 K. The results suggest that the doping with composite approach could boost thermoelectric efficiency in n-type CoSb 3 -based materials.

Influence of synthesis method and processing on the thermoelectric properties of CoSb3 skutterudites

Nanostructuring and Thermoelectric Properties of Bulk Skutterudite Compound Cosb3

Thermoelelctric Properties of Nanostructured Skutterudite-Related Compounds

Significant enhancement of electrical conductivity by incorporating carbon fiber into CoSb3 thermoelectric skutterudite fabricated by spark plasma sintering method

Possible reduction of lattice thermal conductivity in n-type CoSb2.875Te0.125 skutterudite originating from collaborative adjustment between Indium micro and α-WC nano inclusions

Enhanced power factor and suppressed lattice thermal conductivity of CoSb3 Skutterudite by Ni substitution and nanostructuring for high thermoelectric performance

Solvothermal synthesis of nanosized CoSb 3 skutterudite

Thermoelectric Property of Fine-Grained CoSb3skutterudite Compound Fabricated by Mechanical Alloying and Spark Plasma Sintering

CoSb3-based skutterudite nanocomposites prepared by cold sintering process with enhanced thermoelectric properties

Solvothermal Synthesis and Thermoelectric Properties of Skutterudite Compound Fe 0.25 Ni 0.25 Co 0.5 Sb 3

A review of CoSb3-based skutterudite thermoelectric materials

Microstructure and Thermoelectric Properties of CoSb3 Synthesized by MA-SPS Method

Enhanced thermoelectric properties of n-type CoSb3-based composites by incorporating In particles

Thermoelectric Properties of Yb0.15Co4Sb12based Nanocomposites with CoSb3nano-inclusion

Metallization and Diffusion Bonding of CoSb3-Based Thermoelectric Materials

Thermoelectric properties of (Cu,Te) co-doped CoSb 3 synthesized by high-pressure and high-temperature

New synthesis route of highly porous InxCo4Sb12 with strongly reduced thermal conductivity

Effects of Co:Sb Molar Ratio on Synthesis and Properties of Undoped Cosb3 Prepared Via A Polyol Method

Enhanced thermoelectric performance of skutterudite Co1−yNiySn1.5Te1.5−x with switchable conduction behavior

Multiscale Length Structural Investigation and Thermoelectric Performance of Double-Filled Sr0.2Yb0.2Co4Sb12: An Exceptional Thermal Conductivity Reduction by Filler Segregation to the Grain Boundaries

Enhanced thermoelectric performance of Bi2-xCuxS3 by hydrothermal synthesis and spark plasma sintering