Possible reduction of lattice thermal conductivity in n-type CoSb2.875Te0.125 skutterudite originating from collaborative adjustment between Indium micro and α-WC nano inclusions

M. Uday Kumar,R. Swetha,B. V. Sahana,Ramappa S. Kuri,Bogdan Popescu,Ilhame Assahsahi,Latha Kumari

DOI: https://doi.org/10.1007/s10854-024-13713-y

2024-10-26

Journal of Materials Science Materials in Electronics

Abstract:In this work, single-phase Te-doped CoSb 3 polycrystalline bulk (Indium powder) and nanocomposites (α-WC nanopowder) were synthesized via a ball milling, hand-grinding and consolidated by spark plasma sintering technique. The thermoelectric and mechanical characteristics of as-synthesized composites were studied. The electrical resistivity varies between 11.82 and 12.82 μΩ-m for CoSb 2.875 Te 0.125 + x ( x = 0.33% In, 1% In, 2% In, 4% In and 1% In + 0.33% α-WC, respectively) composites. At temperature of 300 K, composite with x = 1% In exhibit the lowest resistivity of 11.82 μΩ-m. Also, negative values of Seebeck coefficients confirm that electrons are the predominant charge carriers. The maximum power factor of 2566 and 2482 μWm −1 K −2 are observed from x = 1% In and x = 1% In + 0.33% α-WC composites at 673 K, respectively. Notably, the power factor of 1% In and 1% In + 0.33% α-WC composites is slightly higher (1.05 times) than the CoSb 2.875 Te 0.125 sample. The composites with lowest weight percent of 1% In and 1% In + 0.33% α-WC have a considerably improved power factor. For the composite with x = 1% In + 0.33% α-WC, the minimum thermal conductivity of 2.32 W/m–K at 300 K was achieved through a combination of doping and dispersion in the CoSb 2.875 Te 0.125 matrix. It is possible that the multi-scale size distributions of grains will reduce the lattice thermal conductivity by scattering phonons over a large wavelength range. As a result, an increased figure of merit of 0.82 was achieved for CoSb 2.875 Te 0.125 + 1% In + 0.33% α-WC composites at 823 K. The results suggest that the doping with composite approach could boost thermoelectric efficiency in n-type CoSb 3 -based materials.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied