Fanfan Shi,Chang Tan,Hongxiang Wang,Xiaojian Tan,Yinong Yin,Bo Yu,Jianfeng Cai,Chenglong Xiong,Guoqiang Liu,Jun Jiang

DOI: https://doi.org/10.1021/acsami.0c15991

2020-11-10

Abstract:Constructing a nanocomposite to introduce a coherent interface is an effective way to improve the property of thermoelectric material. Here, a series composites of Bi_0.48Sb_1.52Te₃–<i>x</i> wt % Sb₂Te₃ (<i>x</i> = 0, 0.3, 0.5, 0.8, and 1.0) were synthesized, where the hydrothermally prepared Sb₂Te₃ nanosheets were intimately wrapped in the solid-state-reacted Bi_0.48Sb_1.52Te₃ matrix. The formation of a coherent interface was observed and confirmed by the scanning electron microscopy characterization. As the Sb₂Te₃ content was over 0.5 wt %, the carrier mobility could increase by 26%, while the carrier concentration decreased by 9% compared to those of the pure matrix at 300 K, enhancing the power factor to 40.1 μW/cm K². Moreover, the Bi_0.48Sb_1.52Te₃–0.5 wt % Sb₂Te₃ sample exhibited a reduced lattice thermal conductivity of 0.83 W/m K at room temperature, resulting from the strengthened phonon scattering by interfaces. Combined with the manipulations of both the electronic and thermal transport by constructing a coherent interface, a maximum <i>ZT</i> of 1.05 was obtained in the <i>x</i> = 0.5 composite at 300 K, and it was improved by 20% compared with the result of the Bi_0.48Sb_1.52Te₃ matrix.This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to improve the performance of thermoelectric materials by constructing nanocomposites, specifically to enhance the thermoelectric performance of p - type Bi₀.₄₈Sb₁.₅₂Te₃/Sb₂Te₃ composites. The main objective of the research is to optimize the electron and heat transport properties by introducing a coherent interface, thereby increasing the power factor (\( \sigma S^2 \)) and the thermoelectric figure of merit (ZT value).

### Specific problem description:

1. **Background problems**:
- The performance of thermoelectric materials is usually evaluated by the dimensionless thermoelectric figure of merit \( ZT=\frac{\sigma S^2 T}{\kappa} \), where \( \sigma \) is the electrical conductivity, \( S \) is the Seebeck coefficient, \( T \) is the operating temperature, and \( \kappa \) is the total thermal conductivity.
- Traditionally, there is an intrinsic correlation among these transport coefficients (electrical conductivity, Seebeck coefficient, and thermal conductivity), and it is difficult to optimize them simultaneously according to the Wiedemann - Franz law.

2. **Research objectives**:
- By adding Sb₂Te₃ nanosheets with different contents (0.3 wt%, 0.5 wt%, 0.8 wt%, and 1.0 wt%) in the Bi₀.₄₈Sb₁.₅₂Te₃ matrix to construct a coherent interface, in order to enhance the thermoelectric performance.
- To study how to filter low - energy carriers through interface potential barriers, increase carrier mobility and reduce lattice thermal conductivity, thereby increasing the power factor and ZT value.

### Solutions:

- **Experimental methods**:
- Sb₂Te₃ nanosheets were synthesized by the hydrothermal method and mixed with Bi₀.₄₈Sb₁.₅₂Te₃ powder prepared by the solid - state reaction, and then the composites were prepared by the hot - pressing method.

- **Result analysis**:
- When the Sb₂Te₃ content was 0.5 wt%, the carrier mobility increased by 26%, the carrier concentration decreased by 9%, and the power factor reached 40.1 μW/cm K².
- The lattice thermal conductivity decreased from 0.88 W/m K of pure Bi₀.₄₈Sb₁.₅₂Te₃ to 0.83 W/m K, which was due to the enhanced phonon scattering at the interface.
- Finally, in the composite with x = 0.5 wt%, the ZT value reached 1.05 at 300 K, which was 20% higher than that of pure Bi₀.₄₈Sb₁.₅₂Te₃.

### Conclusions:

By introducing Sb₂Te₃ nanosheets and constructing a coherent interface, the thermoelectric performance of Bi₀.₄₈Sb₁.₅₂Te₃ can be effectively improved, especially achieving a significant increase in the ZT value at room temperature. This method provides a new idea for the development of high - performance thermoelectric materials.