Abstract:SiOC ceramic modified carbon fiber needled felt preform composites (C-f/SiOC) with densities of 0.4 and 0.7 g/cm(3) were prepared by precursor infiltration and pyrolysis (PIP) method using methyltrimethoxysilane (MTMS) and dimethyldimethoxysilane (DMDMS) as precursors. The densification behavior was investigated through scanning electron microscopy (SEM) analysis of microstructure of C-f/SiOC composites undergoing different PIP times. The results indicate that with increase of PIP times, a great amount of SiOC ceramic was introduced into the preform, completely covering on the carbon fibers and occupying the open pores. The thermal performance, mechanical properties, and oxidation resistance of the composites were studied via various tests. The results illustrate that after two-time PIP procedure, thermal conductivities of the composites are 0.41-2.54 and 1.28-4.04 W/(m.K) in z direction and x/y plane, respectively, at RT-1500 degrees C. The compressive strengths of the composite arrive at 2.1 MPa in z direction and 7.8 MPa in x/y plane, which are almost 3.5 times and 6.5 times, respectively, counterparts of the raw preform. The incorporation of SiOC ceramic can remarkably improve anti-oxidation ability of the composites at 600 degrees C. The oxidation weight loss is merely 2.1 wt% after 60-min oxidation at 600 degrees C.

Crucial roles of egg white liquid in preparing excellent SiC anti-oxidation coatings on carbon felt fibers

Preparation Of Compact And Ultra-Thin Si-Al-C Anti-Oxidation Film On Fibers Of Carbon Felt

SiC Micro-Threads Prepared Within the Carbon Fiber Felt

Oxidation resistance improvement of carbon fiber nonwoven fabrics through SiC coating technology

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

Enhanced antioxidation and microwave absorbing properties of SiC/SiO2 coating on carbon fiber

Influence of SiC Coating on Antioxidation Property of Carbon Fibers

Oxidation protection of carbon fibers by a reaction sintered nanostructured SiC coating

Influence Of Sic Coating On The Oxidation Behavior Of Pan Carbon Fiber At Elevated Temperatures

Theoretical design and preparation of SiC whiskers catalyzed by Fe-oxides on carbon fibers

Critical Role of C/SiO2 Composite Coating in Enhancing the Mechanical and Antioxidation Properties of 3D Needled Carbon Fibers

Fabrication of SiC ultrafine fiber with low oxygen content by electrospinning, thermal curing and pyrolysis of cyano-polycarbosilane

Preparation and oxidation behavious of SiO2 and SiC coating 3-D braided carbon fiber

Improvement of Strength and Oxidation Resistance for SiC/graphite Composites by SiC Coating

Processing Continuous Submicro/Nano SiC Fibers by Electrospinning

Preparation and Properties of SiOC Ceramic Modified Carbon Fiber Needled Felt Preform Composites

Preparation of Silicon Carbide/Graphite Composite Ceramic Sealing Material by Liquid Silicon Inifltration Processing

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites

Fabrication of SiC nanofiber aerogel felt with high-temperature thermal insulation performance

Emulsion-Blow Spun Self-Sustained Crystalline β-Silicon Carbide (SiC) Fiber Mat and Its Conductivity Property

SiC/SiO2 core–shell nanocables formed on the carbon fiber felt