Abstract:This paper focuses on the preparation of boron-containing phenolic resin (BPR)-derived carbon modified three-dimensional (3D) needled carbon fiber reinforced silicon oxycarbide (SiOC) composites through a simple precursor infiltration and pyrolysis process (PIP), and the influence of PIP cycle numbers on the microstructure, mechanical, high-temperature oxidation resistance. The electromagnetic wave (EMW) absorption properties of the composites were investigated for the first time. The pyrolysis temperature played an important role in the structural evolution of the SiOC precursor, as temperatures above 1400 °C would cause phase separation of the SiOC and the formation of silicon carbide (SiC), silica (SiO2), and carbon. The density and compressive strength of the composites increased as the PIP cycle number increased: the value for the sample with 3 PIP cycles was 0.77 g/cm3, 7.18 ± 1.92 MPa in XY direction and 9.01 ± 1.25 MPa in Z direction, respectively. This composite presented excellent high-temperature oxidation resistance and thermal stability properties with weight retention above 95% up to 1000 °C both under air and Ar atmosphere. The minimal reflection loss (RLmin) value and the widest effective absorption bandwidth (EAB) value of as-prepared composites was −24.31 dB and 4.9 GHz under the optimization condition for the sample with 3 PIP cycles. The above results indicate that our BPR-derived carbon modified 3D needled carbon fiber reinforced SiOC composites could be considered as a promising material for practical applications.

Preparation and Properties of SiOC Ceramic Modified Carbon Fiber Needled Felt Preform Composites

Microwave absorption and mechanical properties of SiCf/SiOC composites with SiO2 fillers

Preparation and properties of Ti3SiC2 preform reinforced SiC ceramic matrix composites

Precursor Infiltration and Pyrolysis Cycle-Dependent Microwave Absorption and Mechanical Properties of Lightweight and Antioxidant Carbon Fiber Felts Reinforced Silicon Oxycarbide Composites.

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites

Preparation and Characterization of SiO2/Carbon Foam and SIC/Carbon Foam Composites

Microstructural Regulation, Oxidation Resistance and Mechanical Properties of Cf/SiC/SiHfBOC Composites Prepared by Chemical Vapor Infiltration with Precursor Infiltration Pyrolysis

Oxidation Properties of Three Dimensional (3-D) Carbon Fiber Preform Coated by SiC-SiO<sub>2</sub>

Oxidation Properties of Three Dimensional (3-D) Carbon Fiber Preform Coated by SiC-SiO2

A Low Cost Preparation of C/SiC Composites by Infiltrating Molten Si into Gelcasted Pure Porous Carbon Preform

Fabrication of Co-Continuous SiC/Al Composites from Novel SiC Preforms with High Porosity and Controllable Pore Size

Carbon-bonded Carbon Fiber Composites Reinforced with SiOC-based Polymer Derived Ceramics: Microstructure and Properties

Effect of Pyrocarbon Content in C/C Preforms on Microstructure and Mechanical Properties of the C/C–SiC Composites

Strong and Thermostable Boron-Containing Phenolic Resin-Derived Carbon Modified Three-Dimensional Needled Carbon Fiber Reinforced Silicon Oxycarbide Composites with Tunable High-Performance Microwave Absorption Properties

C/C–SiC Composites Derived from Single‐source Poly(silylene–acetylene) Precursors

Structure and Energetics of SiOC and SiOC‐modified Carbon‐bonded Carbon Fiber Composites

Fabrication and Properties of Lightweight SiOC Modified Carbon-Bonded Carbon Fiber Composites

Fabrication of C/SiC composites by siliconizing carbon fiber reinforced nanoporous carbon matrix preforms and their properties

Improving thermal conductivity of Al/SiC composites by post-oxidization of reaction-bonded silicon carbide preforms

Multifunction properties of SiOC reinforced with carbon fiber and in-situ SiC nanowires

Fabrication and Properties of Reaction-Formed SiC by Infiltrating Molten Si into Mesocarbon Microbeads-Based Carbon Preform