Abstract:Silicon carbide (SiC) whiskers were synthesized by a facile catalyst reaction. Phenolic resin and silicon powders were the raw materials, and cupric nitrate (Cu(NO3)2) was a catalyst precursor under a reducing atmosphere at 1200 °C. The whiskers with Cu(NO3)2 catalyst had a core-shell structure. The inner nanowire had a diameter about 15 nm, and the external structure had a thickness of 38-65 nm. Upon increasing the as-calcined temperature, the thickness of SiO2 shell decreased, and the diameter of the SiC core increased. The copper oxide (CuO) phase derived from Cu(NO3)2 was reduced to copper (Cu) by gases during the process of pyrolysis phenolic resin. Cu played a pivotal role in SiC whiskers formation and its morphology control. The Cu/Si alloy was formed by Cu dissolving with Si, and this step triggered a chain reaction to promote the production of more silicon monoxide (SiO). With the Cu(NO3)2 catalyst, the synthesis mechanism of SiC whiskers transformed from vapor-liquid-solid (V-L-S) to vapor-solid (V-S). The transformation of single carbon bonding phase into C-SiC/SiO2 combined bonding phases to generate much more amount of unique C-SiC/SiO2 interfaces improved the strength and oxidation resistance of the pyrolytic carbons of the phenolic resin.

Theoretical design and preparation of SiC whiskers catalyzed by Fe-oxides on carbon fibers

Effect of Catalyst on the Preparation of Silicon Carbide Whiskers from Silica and Carbon

VLS growth of SiC whisker from FeSi flux

Growth of silicon carbide whiskers in FexSiy flux

Study on growth factors of SiC whisker in situ in SiCW/SiC composites based on selective laser sintering technology

Improving the strength and oxidation resistance of phenolic resin derived pyrolytic carbons via Cu-catalyzed in-situ formation of SiC@SiO2

Synthesis of Bamboo‐like SiC Whiskers from Waste Silica Fume

High Yield Silicon Carbide Whiskers from Rice Husk Ash and Graphene: Growth Method and Thermodynamics

Synthesis and characterization of silicon carbide whisker arrays prepared by thermal evaporation method

Synthesis mechanism of α-Si3N4 whiskers via SiO vapor in reaction bonded Si3N4-SiC composite

The preparation of mullite foamed ceramics reinforced by in-situ SiC whiskers and their reinforcement mechanism

Controllable synthesis of Si@SiC plate@Si3N4 whisker with core-shell structure and their electrochemical performances

Facile growth of oriented SiC nanowires arrays on carbon fiber cloth via CVD

Narrow-chirality distributed single-walled carbon nanotube synthesized from oxide promoted Fe–SiC catalyst

Novel Two-Step Process for Synthesising Β-Sic Whiskers from Coal Fly Ash and Water Glass

Effects of different catalysts on performance of self-bonded SiC refractories

Preparation of Metallic Monolithic Pt/FeCrAl Fiber Catalyst by Suspension Spraying for VOCs Combustion.

Growth of SiC nanowires/nanorods using a Fe–Si solution method

In Situ Catalytic Synthesis of Si3N4 Nanowhiskers Reinforced SiC Refractories and Their High-Temperature Properties

A New Route to Synthesize SiC−AlN Solid Solution Whiskers

3D-SiC decorated with SiC whiskers: Chemical vapor infiltration on the porous 3D-SiC lattices derived from polycarbosilane-based suspensions