Abstract:Carbon-bonded alumina (Al2O3–C) refractories were fabricated using unmodified (3–1, 1–0, and 0.045 mm) and Si powder-modified tabular alumina aggregates (3–1 mm) as raw materials, in addition to Si powder, ultra-fine α–Al2O3 powder, and carbon black as fines, and a thermosetting phenolic resin as the binder. The microstructures and phase compositions of the samples were analyzed by scanning electron microscopy and X-ray diffraction. After the mixing and wearing test, the Si powder-modified tabular alumina aggregates exhibited a low Si powder dropping ratio, thereby meeting the requirements to prepare Al2O3–C refractories. The addition of Si powder-modified tabular alumina aggregates to the material had little effect on the thermal shock resistance of the Al2O3–C refractory and was beneficial to improving the cold modulus of rupture of the material. Since the surface of the added modified aggregate was not dense, diffusion and mass transfer were promoted during the oxidation process, thereby leading to a slight decrease in the oxidation resistance of the material. The introduction of Si powder-modified tabular alumina aggregates increased the amount of Si powder particles surrounding the aggregates, resulting in the in situ generation of additional SiC fibers during high temperature heat treatment. Ultimately, this strengthened the interfacial bonding between the matrix and the aggregates. In addition, compared with the hot modulus of rupture (HMOR) of sample S0 (containing 50 wt.% tabular alumina aggregates), the HMOR of sample S2 (containing 51 wt.% modified tabular alumina aggregates with 1 wt.% Si powder coating) was 30% higher.

Effects of different catalysts on performance of self-bonded SiC refractories

Catalytic Preparation of Si3N4-Bonded SiC Refractories and Their High-Temperature Properties

In Situ Catalytic Synthesis of Si3N4 Nanowhiskers Reinforced SiC Refractories and Their High-Temperature Properties

Effect of three catalysts on synthesis of silicon carbide whiskers with silica fume

Effect of Catalyst on the Preparation of Silicon Carbide Whiskers from Silica and Carbon

Catalytic Nitridation Preparation of High-Performance Si3N4(w)-SiC Composite Using Fe2O3 Nano-Particle Catalyst: Experimental and DFT Studies

Si3N4-SiCpComposites Reinforced Byin SituCo-Catalyzed Generated Si3N4Nanofibers

Preparation of SiC/multilayer graphene composite ceramic with improved properties catalyzed by Ni nanoparticle

Preparation and properties of alumina-carbon castables using SiC nanofiber coated graphite flake

Improving the strength and oxidation resistance of phenolic resin derived pyrolytic carbons via Cu-catalyzed in-situ formation of SiC@SiO2

Theoretical design and preparation of SiC whiskers catalyzed by Fe-oxides on carbon fibers

Controllable synthesis of Si@SiC plate@Si3N4 whisker with core-shell structure and their electrochemical performances

Effect of SiC Nano-Whisker Addition on WC–Ni Based Cemented Carbides Fabricated by Hot-Press Sintering

Study on growth factors of SiC whisker in situ in SiCW/SiC composites based on selective laser sintering technology

In-situ synthesis of Fe Si phases and their effects on the properties of SiC porous ceramics

In Situ Synthesis and Interfacial Bonding Mechanism of SiC in MgO–SiC–C Refractories

Effect of silicon powder-modified tabular alumina aggregates on the mechanical properties and microstructures of carbon-bonded alumina refractories

Effect of SiC Nano-Whisker Addition on TiCN-based Cermets Prepared by Spark Plasma Sintering

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering

Preparation and Properties of SiC Refractories Via Carbonization-Nitridation Reaction

Improved thermal shock stability and oxidation resistance of low-carbon MgO–C refractories with introduction of SiC whiskers