Abstract:Features peculiar to the synthesis of SiC–Si 3 N 4 –Si 2 N 2 O composite powder with a controlled content of silicon carbide, nitride, and oxynitride phases, as well as the structure and properties of hot-pressed ceramics produced from this powder, were examined. The optimal composition of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O powder was achieved by heating a 1 : 3 mixture of thermally expanded graphite (TEG) and silicon up to 1200°C in air. The interaction of TEG with fine silicon at 1200°C led to the formation of a solid solution of carbon in silicon carbide, accompanied by heat release. The generated heat increased temperature within localized volumes of the TEG cellular structure to a level where air nitrogen facilitated the development of silicon nitride and oxynitride and an amorphous phase. The amorphous phase crystallized as the interaction time increased to 2.5 h. The duration of the process influenced the final distribution of the phases, formed with the participation of CO, SiO, and air nitrogen. The microstructure of the synthesized powder was characterized by a general agglomerated state, resulting from rod and plate forms of Si 3 N 4 and Si 2 N 2 O. Hot pressing of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O composite powder with Al 2 O 3 and Y 2 O 3 activators yielded superfine ceramics, possessing enhanced hardness and fracture toughness (HV10 = 20.7 GPa and K Ic = 6.5 MPa · m 1/2 ). The structure of the ceramics sintered at 2000°C differed from those sintered at 1850°C, primarily by higher density and average grain size. The superfine state significantly influenced the abrasive wear resistance of the ceramics in dry friction conditions. The linear wear index of a sample with an average size of structural elements varying from 0.2 to 1.5 μm was 111 μm/km at a sliding speed of 1 m/sec under a load of 0.2 MPa. This was significantly lower than the linear wear index of industrial ceramics of reaction-sintered silicon carbide (RSSC), which was 232.4 μm/km.

Catalytic Preparation of Si3N4-Bonded SiC Refractories and Their High-Temperature Properties

In Situ Catalytic Synthesis of Si3N4 Nanowhiskers Reinforced SiC Refractories and Their High-Temperature Properties

Effects of different catalysts on performance of self-bonded SiC refractories

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Fabrication of novel AlN-SiC-C refractories by nitrogen gas-pressure sintering of Al4SiC4

Liquid-Phase-Assisted Catalytic Nitridation of Silicon and In Situ Growth of α-Si3N4

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering

Synthesis mechanism of AlN–SiC solid solution reinforced Al2O3 composite by two-step nitriding of Al–Si3N4–Al2O3 compact at 1500 °C

Preparation of Si3N4–TiN–SiC composite by partial substitution of Ti–Si–Fe alloy for Si under N2 atmosphere

Enhanced mechanical properties of R–SiC honeycomb ceramics with in situ AlN–SiC solid solution

Influence of ceramic phase content and its morphology on mechanical properties of MgO–C refractories under high temperature nitriding

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

Formation of Nanocarbon Structures in MgO–C Refractories Matrix: Influence of Al and Si Additives

Preparation and properties of alumina-carbon castables using SiC nanofiber coated graphite flake

Enhancement of oxidation resistance at 1000–1400 °C of low carbon Al2O3–C refractories with pre-synthesized SiCnw/Al2O3

Fabrication of high performance silicon nitride ceramics with TiO2 additive by annealing process

Improvement in high-temperature oxidation resistance of SiC nanocrystalline ceramics by doping AlN

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Inhibiting crystallization of fused silica ceramic at high temperature with addition of α-Si3N4

In-situ formation of plate-like Al4O4C and MWCNTs in Al2O3–C refractories with Al4SiC4 additives