Inhibiting crystallization of fused silica ceramic at high temperature with addition of α-Si3N4

Jun Liu,Qinghu Wang,Yawei Li,Xiong Liang,Xueqing Wang,Shaobai Sang,Liping Pan,Yibiao Xu

DOI: https://doi.org/10.1016/j.ceramint.2020.12.266

IF: 5.532

2021-04-01

Ceramics International

Abstract:Fused silica (SiO2) ceramic crucibles with α-Si3N4 coating are commonly used for smelting photovoltaic silicon (Si). However, SiO2 ceramics will inevitably undergo crystallization and large volume change during the high-temperature service, which will lead to crucible cracking and deteriorate the quality and yield of the Si ingot. In this work, α-Si3N4/SiO2 ceramics are fabricated by introducing α-Si3N4 into SiO2 ceramics to inhibit crystallization. The results show that the introduction of α-Si3N4 can effectively inhibit crystallization of SiO2 ceramics at temperature higher than 1450 °C. Only 5 wt% cristobalite form in SiO2 ceramic with 20 wt% α-Si3N4 (heated at 1550 °C for 30min). The crystallization activation energy of SiO2 ceramic containing 20 wt% α-Si3N4 increases by 2.27 times to 931.2kJ/mol compared with that of pure SiO2 ceramic (409.6kJ/mol). The inhibition crystallization effect and increased activation energy derive from the in-situ formation of O–Si–N chemical bond and physical isolation of SiO2 particles by α-Si3N4 powders.

materials science, ceramics