Abstract:Silicon carbide (SiC) whiskers were synthesized by a facile catalyst reaction. Phenolic resin and silicon powders were the raw materials, and cupric nitrate (Cu(NO3)2) was a catalyst precursor under a reducing atmosphere at 1200 °C. The whiskers with Cu(NO3)2 catalyst had a core-shell structure. The inner nanowire had a diameter about 15 nm, and the external structure had a thickness of 38-65 nm. Upon increasing the as-calcined temperature, the thickness of SiO2 shell decreased, and the diameter of the SiC core increased. The copper oxide (CuO) phase derived from Cu(NO3)2 was reduced to copper (Cu) by gases during the process of pyrolysis phenolic resin. Cu played a pivotal role in SiC whiskers formation and its morphology control. The Cu/Si alloy was formed by Cu dissolving with Si, and this step triggered a chain reaction to promote the production of more silicon monoxide (SiO). With the Cu(NO3)2 catalyst, the synthesis mechanism of SiC whiskers transformed from vapor-liquid-solid (V-L-S) to vapor-solid (V-S). The transformation of single carbon bonding phase into C-SiC/SiO2 combined bonding phases to generate much more amount of unique C-SiC/SiO2 interfaces improved the strength and oxidation resistance of the pyrolytic carbons of the phenolic resin.

Growth of silicon carbide whiskers in FexSiy flux

VLS growth of SiC whisker from FeSi flux

Ultrafast growth of single-crystalline Si nanowires

Theoretical design and preparation of SiC whiskers catalyzed by Fe-oxides on carbon fibers

Effect of Catalyst on the Preparation of Silicon Carbide Whiskers from Silica and Carbon

SiC Crystal Growth from Transition Metal Silicide Fluxes

Synthesis of Bamboo‐like SiC Whiskers from Waste Silica Fume

Novel Two-Step Process for Synthesising Β-Sic Whiskers from Coal Fly Ash and Water Glass

Growth of SiC nanowires/nanorods using a Fe–Si solution method

Synthesis and characterization of silicon carbide whisker arrays prepared by thermal evaporation method

High Yield Silicon Carbide Whiskers from Rice Husk Ash and Graphene: Growth Method and Thermodynamics

Study on growth factors of SiC whisker in situ in SiCW/SiC composites based on selective laser sintering technology

A New Route to Synthesize SiC−AlN Solid Solution Whiskers

Effects of different catalysts on performance of self-bonded SiC refractories

Synthesis of 2H-Sic Whiskers by Decomposition of Si<sub>3</sub>N<sub>4</sub>

Combustion Synthesis of Β-Sialon Whiskers

Direct observation of the growth process of silicon carbide nanowhiskers by vapor–solid process

Synthesis, characterization and growth mechanism of SiC fibers

Improving the strength and oxidation resistance of phenolic resin derived pyrolytic carbons via Cu-catalyzed in-situ formation of SiC@SiO2

The Growth of Sic Crystals from Cosi Molten Alloy Fluxes

Growth of platelike and branched single-crystalline Si3N4 whiskers