Microstructure and mechanical properties of AlN–hBN based machinable ceramics prepared by pressureless sintering
W.S. Cho,Z.H. Piao,K.J. Lee,Y.C. Yoo,J.H. Lee,M.W. Cho,Y.C. Hong,K. Park,W.S. Hwang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2006.05.044
IF: 5.7
2007-01-01
Journal of the European Ceramic Society
Abstract:AlN based machinable ceramics containing hBN were prepared by economical pressureless sintering at 1800°C for 2h in a nitrogen gas atmosphere. The effects of hBN content on microstructure, mechanical properties and machinability were investigated. The relative density of sintered compacts decreased with increasing hBN content. The four-point flexural strength of 340MPa for monolithic AlN also decreased to about 120MPa by the addition of 20vol% hBN, mainly due to increased porosity. With increasing hBN content, AlN–hBN based ceramic composites revealed increased crack deflection. The Vickers indentation crack paths in specimens were sinusoidal indicating crack bridging and pull-outs of composite grains during crack propagation. During end-milling and microdrilling processes for AlN ceramic composites with more than 10vol% hBN, measured feed and thrust forces decreased with increasing hBN content, demonstrating a good machinability of the composites.
materials science, ceramics