Fabrication and properties of the machinable B4C/BN composites ceramics

Jiang Tao,Jin Zhihao,Qiao Guanjun
DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.z3.141
2007-01-01
Rare Metal Materials and Engineering
Abstract:The machinable B4C/BN composites ceramics were fabricated by hot-pressing sintering process with sintering temperature of 1850 degrees C, the pressure of 30 MPa and holding time of 1 h. Effects of the h-BN content on the mechanical properties and machinability of the B4C/BN composites were investigated, and the phase composition and microstructure of the B4C/BN composites were investigated by X-ray diffraction and SEM, respectively. The experimental results showed that, with h-BN content increasing, the density of composites decreased gradually resulting in corresponding decrease in fracture strength and fracture toughness of the composites; and the Vickers hardness of composites decreased gradually, while the machinability was improved noticeably. When the h-BN content was more than 20%, the B4C/BN composites exhibited excellent machinability.
What problem does this paper attempt to address?