Fabrication and Properties of Machinable TZP-BN-10%Si3N4 Ceramic Composites

李永利,乔冠军,金志浩

DOI: https://doi.org/10.3321/j.issn:0253-987X.2003.05.018

2003-01-01

Abstract:TZP-BN-10% Si3N4 ceramic composites, whose volume fraction is 0,5%, 10%, 15% ,20% ,30% and 40%, respectively, were fabricated by hot-pressing the powder mixture of TZP (zirconia tetragonal polycrystal), h-BN and 10% mass fraction of Si3N4. It is found that the composites with BN volume fraction over 15% have a good machinability, namely, the composites can be machined by WC metal tools. Vickers hardness of the composites decreases with h-BN content. With the increase of the BN volume fraction, both bending strength and fracture toughness of the composites show a slow decrease when BN volume fraction is less than 20% and a steep decrease when BN volume fraction is over 20%. The composite possesses the combination of high mechanical properties and excellent machinability when BN volume fraction equals 20%-the bending strength is 637 MPa, the fracture toughness is 9.22 MPa · m1/2, and the drilling rate is more than 2 mm/min. Drilling rates and normal forces are used to evaluate the machinability of these materials.