Abstract:In the present paper, the ZrB2/h-BN multiphase ceramics were fabricated by SPS (spark plasma sintering) technology at lower sintering temperature using h-BN, ZrO2, AlN and Si as raw materials and B2O3 as a sintering aid. The phase constitution and microstructure of specimens were analyzed by XRD and SEM. Moreover, the effects of different sintering pressures on the densification, microstructure and mechanical properties of ZrB2/h-BN multiphase ceramics were also systematically investigated. The results show that the ZrB2 was obtained through solid phase reaction at different sintering pressures, and increasing sintering pressure could accelerate the formation of ZrB2 phase. As the sintering pressure increasing, the fracture strength and toughness of the sintered samples had a similar increasing tendency as the relative density. The better comprehensive properties were obtained at given sintering pressure of 50MPa, and the relative density, fracture strength and toughness reached about 93.4%, 321MPa and 3.3MPa·m1/2, respectively. The SEM analysis shows that the h-BN grains were fine and uniform, and the effect of sintering pressure on grain size was inconspicuous. The distribution of grain is random cross array, and the fracture texture was more obvious with the increase of sintering pressure. The fracture mode of sintered samples remained intergranular fracture mechanism as sintering pressure changed, and the grain refinement, grain pullout and crack deflection helped to increase the mechanical properties.

Densification mechanism and corrosion resistance of h-BN/ZrO 2 ceramics prepared by spark plasma sintering

Effect of ZrO2 on sintering behavior and properties of h-BN/ZrO2 composites by spark plasma sintering

Rapid densification mechanism and properties of h-BN/ZrO 2 composites with oxide additives by spark plasma sintering

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

High temperature oxidation resistance of hot-pressed h-BN/ZrO 2 composites

Microstructure, mechanical properties and thermal shock behavior of h-BN-SiC ceramic composites prepared by spark plasma sintering

Mechanical and tribological properties of h-BN/ZrO2/SiC solid-lubricating ceramic composites

Microstructure and Mechanical Properties of ZrB2/h-BN Multiphase Ceramics by Low-Temperature Reactive Sintering

High-pressure Synthesis of Al2O3-cBN Composites: Effect of Thermodynamic Condition and Cbn Volume Fraction on Their Microstructure and Properties

Fabrication of (Zr,Ti)B2-ZrN-BN composites through reactive spark plasma sintering of ZrB2 and TiN

Role of h-BN content on microstructure and mechanical properties of hot-pressed ZrB2–SiC composites

Processing and Mechanical Properties of Zirconium Diboride‐Based Ceramics Prepared by Spark Plasma Sintering

Analysis of Mechanical Properties of Al2O3‐cBN‐hBN Composites and Identification of Main Influencing Factors

Densification and mechanical properties of boron carbide prepared via spark plasma sintering with cubic boron nitride as an additive

Preparation and Mechanical Properties of Laminated Zirconium Diboride/molybdenum Composites Sintered by Spark Plasma Sintering

Beneficial effect of low BN additive on densification and mechanical properties of hot-pressed ZrB2–SiC composites

Incorporation of BN-coated carbon fibers into ZrB2/SiBCN ceramic composites and their ablation behavior

Mechanical Properties and Microstructure of in Situ Synthesized ZrB 2 -Zrn 1− X Composites

Corrosion resistance of BN–ZrO2 ceramics with different additives by molten steel

The Fabrication and Mechanical Properties of SiC/ZrB2 Laminated Ceramic Composite Prepared by Spark Plasma Sintering