Abstract:To further improve the thermal shock resistance and ablation resistance of SiBCN system ceramics targeted much harsh environment, both ultra-high temperature ceramic phases and carbon fibers are expected to be incorporated simultaneously as the reinforcements. However, tough problems like difficulty in densification as well as degradation of C fibers (Cf) due to interfacial reaction usually cannot be avoided. Thus, in this study, Zr as well as chopped Cf with BN coating were introduced into SiBCN ceramics by mechanical alloying and after hot-pressing sintering to prepare C/SiBCNZr composites. The structure and phase component development have been characterized in detail by XRD, SEM, TEM and XPS etc., and mechanical properties, fracture behavior and toughening mechanisms were also investigated. Zr-B and Zr-O bonds are detected besides Si-C, N-B and N-B-C bonds when pre-alloyed ZrB2 amorphous powder was incorporated into SiBCN system by further mechanical-alloying treatment. After hot-pressing, the ultra-high temperature phases of ZrB2 and ZrN were formed as expected besides the original matrix phases of BN(C) and SiC. Excellent mechanical properties can be obtained for SiBCNZr ceramic. The BN coating on carbon fibers successfully avoids the severe fiber degradation and makes it possible for moderating strong interface bonding, which ensuring the debonding, crack deflection, fiber pulling-out and bridging during the fracture. As a result, the C/SiBCNZr composites retain good mechanical properties and fractures in a pseudoplastic fracture manner, showing better potential applications in harsh environments. Optimization of the BN coating on Cf and Zr incorporation by pre-mechanical alloying can be a good route to achieve Cf/SiBCNZr composites with a better balance between thermal shock resistance, ablation resistance and mechanical properties.

Incorporation of BN-coated carbon fibers into ZrB2/SiBCN ceramic composites and their ablation behavior

Effects of Zr and chopped C fiber on microstructure and mechanical properties of SiBCN ceramics

Ablation properties and mechanisms of BN-coated Cf-reinforced SiBCNZr ceramic composites under an oxyacetylene combustion torch

Synthesis of coatings on SiC fibers and their effects on microstructure and mechanical properties of SiC f /SiBCN composites

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Ablation behavior of Csf/SiC‐BN composites with polyborosilazane as sintering aids: High‐temperature damage mechanism

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Processing, microstructure, and mechanical properties of chopped SiC fibers reinforced ZrB2–hBN–based composites

Ablation behaviour of Csf/ZrB2-SiC composites fabricated by direct ink writing and reactive melt infiltration

Effect of Zr on the solid sintering process of SiBCN ceramics: Diffusion couple method experiment and DFT calculation

Effect of BN interfacial layer on the mechanical behavior of SiC fiber reinforced SiC ceramic matrix composites

Effect of carbon nanotube on processing, microstructural, mechanical and ablation behavior of ZrB2-20SiC based ultra-high temperature ceramic composites

Enhanced ablative resistance of C/C composites with densified ZrB 2 -based ceramics by incorporation of Mo as interface layer

Ablation behavior and mechanisms of 3D Cf/ZrB2-SiC composite applied in long-term temperature up to 2400 °C

Structural characteristics and ablative behavior of C/C–ZrC–SiC composites reinforced with “Z-pins like” Zr–Si–B–C multiphase ceramic rods

Densification mechanism and corrosion resistance of h-BN/ZrO 2 ceramics prepared by spark plasma sintering

Toughening and ablation mechanism of Si3N4 short fiber toughened ZrB2-based ceramics

Mechanical and thermal shock properties of C f /SiBCN composite: Effect of sintering densification and fiber coating

Fabrication and Properties of Short Carbon Fiber-ZrB2 Ceramic Matrix Composites

Effect of Nano SiC on Microstructure and Mechanical Properties of BN-ZrO2-SiC Multiphase Ceramics

Enhanced ablation resistance of HfB2-HfC/SiBCN ceramics under an oxyacetylene torch environment