Abstract:By regulating the proportion of large and small boron nitride particles, BN-ZrO2-SiC composites with particle gradation are designed. Through the strategy of particle grading, small particles could be filled into the “card-house structure” formed by h-BN with large particle size, promoting the densification process. At the same time, this also shortens the mass transfer distance between particles, which is conducive to the mass transfer during the hot-pressing sintering. On the basis of achieving the second phase strengthening effect, the performance of hexagonal boron nitride composite has been further improved. The results demonstrate that by a volumetric proportionality of 6:4 between the constituent large particle (7 μm) and small (1 μm) particle. Thus, the BN-ZrO2-SiC composite with high density has been successfully fabricated at a sintering temperature of 1700°C under 25MPa. The optimization mechanical properties of BN-ZrO2-SiC composites are achieved when the volumetric ratio of large particle (7 μm) to small (1 μm) particle is 6:4. The optimal flexural strength, fracture toughness, Vickers’ hardness and elastic modulus is 187 ± 4 MPa, 2.2 ± 0.3 MPa·m1/2, 0.74 ± 0.06 GPa, and 57 ± 1.1 GPa, respectively. Comparing to the h10 and H10 sample, the thermal conductivity of samples with particle size gradation has been improved, especially the H8h2 and H4h6 samples. The thermal conductivity is significantly enhanced from 14.79 W/(m·K) to 16.83 W/(m·K).

Role of h-BN content on microstructure and mechanical properties of hot-pressed ZrB2–SiC composites

Beneficial effect of low BN additive on densification and mechanical properties of hot-pressed ZrB2–SiC composites

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Microstructure and Mechanical Properties of Reactive Hot-Pressed BN-ZrB_2-ZrO_2 Composites

Effect of BN grain size on microstructure and mechanical properties of the ZrB2–SiC–BN composites

High temperature oxidation resistance of hot-pressed h-BN/ZrO 2 composites

Microstructure and mechanical properties of hot pressed ZrC-SiC-ZrB 2 composites

Mechanical Properties and Microstructure of in Situ Synthesized ZrB 2 -Zrn 1− X Composites

Microstructure, mechanical properties and thermal shock resistance of hot-pressed ZrO2(3Y)-BN composites

Pressureless sinterability study of ZrB2–SiC composites containing hexagonal BN and phenolic resin additives

Microstructure and room/elevated-temperature mechanical properties of hot-pressed h-BN composite ceramics with La2O3-Al2O3-SiO2 addition

Microstructure and Mechanical Properties of ZrB2-SiC Composites

The Effect of Particle Size Gradation on the Microstructure, Mechanical and Thermal Physical Properties of BN-ZrO2-SiC Composites

MICROSTRUCTURE, MECHANICAL PROPERTIES AND FRICTION/WEAR BEHAVIOR OF HOT-PRESSED Si₃N₄/ BN CERAMIC COMPOSITES

Densification and mechanical properties of boron carbide prepared via spark plasma sintering with cubic boron nitride as an additive

A TEM study of nanostructures and interfaces in the hot-press sintered ZrB2–SiC–Si3N4 composites

Investigation on the preparation and machinability of the B4C/BN nanocomposites by hot-pressing process

Mechanical and tribological properties of hot-pressed h-BN/Si3N4 ceramic composites

Inhibiting Effect of Additives on Formation of ZrC Phase in ZrB2–BN Composites by Reactive Hot Pressing

In Situ Preparation and Mechanical Properties of (ZrB2+ZrC)/Zr3[Al(Si)]4C6 Composites

Mechanical and wear properties of h-BN/Si3N4 ceramic composites