Abstract:By employing an in-situ reaction pressureless sintering method, self-reinforced and SiC-B4C-ZrB2 multiphase composites were successfully prepared. The effect of TiO2 and ZrO2 additions on the sintered density, microstructure, and mechanical properties of the composites was investigated. TiO2 and ZrO2 were completely transformed into TiB2 and ZrB2 phases during the sintering process, and their appropriate addition helped enhance the relative density of the composites. In the SiC-B4C-TiB2 (SBT) composite, the introduction of TiB2 facilitated grain growth in all phases. The composite with 12 vol% TiB2 (SBT12) exhibited optimal mechanical properties, with Vickers hardness, fracture toughness, and flexural strength reaching 30.1±0.8 GPa, 5.17±0.23 MPa·m1/2, and 491±24 MPa, respectively. In the SiC-B4C-ZrB2 (SBZ) composite, the presence of ZrB2 resulted in the formation of a ternary eutectic liquid phase, SiC-B4C-ZrB2, during the sintering process, leading to grain coarsening and the generation of plate-like SiC grains. Among them, the composite with 6 vol% ZrB2 (SBZ6) demonstrated the best overall performance, with Vickers hardness, fracture toughness, and flexural strength of 29.7±0.6 GPa, 6.17±0.36 MPa·m1/2, and 443±22 MPa, respectively. Additionally, SBZ9 exhibited the highest fracture toughness, reaching 6.43±0.44 MPa·m1/2, with the pull-out of plate-like grains considered as the primary contributing factor. This study provides a reference for the preparation of high-strength and tough SiC-B4C-MeB2 multiphase composites through low-temperature pressureless sintering.

Rapid densification mechanism and properties of h-BN/ZrO 2 composites with oxide additives by spark plasma sintering

Densification mechanism and corrosion resistance of h-BN/ZrO 2 ceramics prepared by spark plasma sintering

Effect of ZrO2 on sintering behavior and properties of h-BN/ZrO2 composites by spark plasma sintering

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

High temperature oxidation resistance of hot-pressed h-BN/ZrO 2 composites

Spark plasma sintering and mechanical properties of Al_2O_3-ZrO_2 nanocomposites

Densification, microstructure and mechanical properties of ZrB2–SiCw ceramic composites

Beneficial effect of low BN additive on densification and mechanical properties of hot-pressed ZrB2–SiC composites

SPS densification and ablative performance of ZrB2–SiC–ZrC composites derived from the ternary powders by sol-gel

The Effect of Particle Size Gradation on the Microstructure, Mechanical and Thermal Physical Properties of BN-ZrO2-SiC Composites

Microstructure, mechanical properties and thermal shock behavior of h-BN-SiC ceramic composites prepared by spark plasma sintering

Processing and Mechanical Properties of Zirconium Diboride‐Based Ceramics Prepared by Spark Plasma Sintering

The Effect of Tio2 and Zro2 Additives on the Density, Microstructure, and Mechanical Properties of Pressureless Sintered Sic-B4c

Effect of ZrO2 content on microstructure, mechanical properties and thermal shock resistance of (ZrB2+3Y-ZrO2)/BN composites

Effect of Nano SiC on Microstructure and Mechanical Properties of BN-ZrO2-SiC Multiphase Ceramics

Mechanical, Wetting and Corrosion Properties of a Zr-based Amorphous Alloy Composite Consolidated by Spark Plasma Sintering

Role of h-BN content on microstructure and mechanical properties of hot-pressed ZrB2–SiC composites

Low-Temperature Sintering Behavior and Mechanical Properties of Bn-Zro2-Sic Composites

Mechanical, Corrosion and Wear Characteristics of Cu-Based Composites Reinforced with Zirconium Diboride Consolidated by SPS

Spark Plasma Sintering and Mechanical Properties of ZrO2(Y2O3)–Al2O3 Composites