Abstract:BN/B4C micro-composite and BN/B4C nano-composite were fabricated by hot-pressing process. The thermal shock resistances of the BN/B4C micro-composite and the BN/B4C nano-composite were investigated by the water-quenching method compared with the B4C monolith ceramic. The residual fracture strength after thermal shock test was measured by the three-point bending method. The results show that the thermal shock resistances of the BN/B4C micro-composite and the BN/B4C nano-composite are much better than that of the B4C monolith ceramic. The thermal shock resistance of the BN/B4C nano-composite is much better than that of the BN/B4C micro-composite. The high thermal shock resistances of the BN/B4C micro-composite and the BN/B4C nano-composite can be attributed to their high fracture strength and low modulus of elasticity modulus. The microstructure analysis shows that the weak interface of BN/B4C and cleavage behavior of laminate-structured h-BN particles can remarkably improve the thermal shock resistance of the BN/B4C composites.

FABRICATION AND THERMAL SHOCK RESISTANCE OF THE MACHINABLE BN/B4C COMPOSITE CERAMICS