Effects of Initial Compositions and Nitrogen Flow Rate on TiN/β′-sialon Powder Synthesized from High Titania Slag

李江,薛向欣,姜涛,巫俊斌,段培宁
DOI: https://doi.org/10.3321/j.issn:1001-9731.2008.06.035
2008-01-01
Abstract:Based on the thermodynamic analyses,conductive ceramics powder of TiN/β′-sialon was synthesized by carbothermal reduction-nitridation using high titania slag as the main starting material.The influence of various reaction parameters such as nitrogen flow rate,titanium dioxide content and carbon content on the synthesis of powder have been investigated systematically by X-ray diffraction,scanning electron microscope and energy dispersive X-ray analysis.Powder synthesized in the optimizing process parameter is identified.The results indicate that the products of reaction are more sensitive to the titanium dioxide content and nitrogen flow rate.The proportion of matrix phase and function phase can be adjusted by the amount of titanium dioxide.The best transformation occurred at 1400℃ for 2h under the nitrogen flow rate of 400ml/min with stoichiometric amount carbon.The main phase of the production are β′-sialon and TiN and less amount of 15R and Al2O3 are also found.β′-sialon in the sample exhibit elongated grain morphology as the TiN particles show granular morphology.
What problem does this paper attempt to address?