Abstract:In this investigation, a series of Na0.5Bi0.47Sr0.02TiO3-δ samples are sintered from1000 to 1100°C, were synthesized utilizing the solid-state method. The XRD results indicate that all samples exhibit a perovskite phase, with the exception of those sintered at 1100 °C, which display no discernible impurity peaks.The SEM results indicate that the average grain size exhibits an increase proportionate to the sintering temperature,which attributes to the variations in the actual Na/Bi ratio. From the study of grain conductivity we can obtain that the dominant factor affecting grain conductivity is the activation energy.At 1100°C,the oxygen vacancy concentration emerges as the primary determinant of grain conductivity. It should be noticed that the phase transition temperature of the sample increases (350°C→400°C) with the increase of sintering temperature, which is due to the local A-site disorder aggravated by high temperature sintering. Therefore, reducing the sintering temperature is beneficial to improve the grain conductivity. The grain boundary conductivity initially rises, then diminishes with increasing sintering temperature.It is evident that the enhanced macroscopic grain boundary conductivity stems from a marked reduction in space charge potential within the 1000-1025°C temperature range. Within the 1050°C-1100°C temperature range,the space charge potential barely changed,the significant decrease of intrinsic grain boundary conductivity can be attributed to the surge in the coverage ratio of grain boundary impurities and the number of grain boundary impurities increased caused by the rapid reduction of grain boundary area and thermal evaporation.The research on electrical performance of NBT-based oxygen-ion conductors will promote the application of NBT-based oxygen ion conductors in solid oxide fuel cells, oxygen sensors and other fields.

The Effect of Calcination Temperature and Salt Quantity on Anisotropic Microstructure of Bi4Ti3O12 Powder Prepared by Molten Salt Methods

Influence of Annealing Temperature on Microstructure and Phase Transformations of Oxide System Bi2O3/TiO2 Formed in Aqueous Solutions

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Effects of Process Parameters on Bi4 Si3 O12 Powders Synthesized by Molten Salt Method

Anisotropic Properties of Grain Orientated Bismuth Titanate Ceramics by Spark Plasma Sintering

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

Effect of Cr2O3 and Sintering Temperature on the Property of Aluminum Titanate Prepared with Alumina-Titania Slag

Synthesis of Pure Bi<sub>12</sub>SiO<sub>20</sub> Powder by Molten Salt Method

Synthesis and properties of high aspect ratio SrBi 4 Ti 4 O 15 microplatelets

Molten salt synthesis of Bi2SiO5 powders based on uniform experiment

Study of the synthetic process of CaBi2Ta2O9 powder by the molten‐salt method

Molten Salt Synthesis of Bismuth Ferrite Nano‐ and Microcrystals and Their Structural Characterization

Effect of Er2O3 addition and calcining temperature on CaTiO3 material prepared by solid reaction

Effect of Sintering Temperature on Microstructure and Electrical Properties of Na0.5Bi0.47Sr0.02TiO3-δ Ceramics

Synthesis of Large Diameter Plat-Like Ca3co4o9 Particle by Molten Salt Method

The Effect of Calcination Temperature on the Structure and Performance of Nanocrystalline Mayenite Powders

Effect of SiO2/Al2O3 ratio on sintering behavior, crystallization behavior and properties of diopside-anorthite glass-ceramics

Sintering and Microstructure of BaTiO3 Nano Particles Synthesized by Molten Salt Method

Synthesis of Ba0.6Sr0.4TiO3 Platelet Crystals Based on Bi4Ti3O12 Precursor by Topochemical Microcrystal Conversion

Low temperature synthesis of plate-like Na0.5Bi0.5TiO3 via molten salt method