Abstract:Highlights • Sol-gel glass encapsulation was used to inhibit nanocrystals growth during sintering. • Sol-gel glass encapsulation can promote sintering and improve the dielectric loss. • Hydrolysis of BT in the sol was adverse to the sinter and dielectric properties. Barium titanate (BaTiO 3 , BT) is one of the key dielectric materials for multilayer ceramic capacitor (MLCC) industry. To meet the development trend of miniaturization and high capacity of MLCC, the sintered ceramic with nanosized grain is required. Herein, we demonstrate a controllable preparation of fine-grain BaTiO 3 ceramic by using sol-gel glass encapsulation strategy to suppress the growth of nanocrystal during sintering. It is found that the BaTiO 3 nanocrystal with average lateral particle size of 70 nm and 200 nm (BT70 and BT200) can be coated with Bi 2 O 3 -B 2 O 3 -SiO 2 (BBS) glass shell to form core-shell structures. The fine crystal of barium titanate ceramics can be achieved under different encapsulation quantities and sintering temperature. However, BT70, with a larger specific surface area, higher reactivity, and lower crystallinity, was more prone to hydrolyze in the sol-gel process, leading to the formation of a new phase after sintering, Ba 2 TiSi 2 O 8 , which adversely affected both the sintering behavior and dielectric properties. On the other hand, BT200 exhibited lower possibility to hydrolyze in the sol-gel process, resulting in single-phase ceramics after sintering. When the BT200 coated with 5% (in mass) BBS was sintered at 1100 °C, a dense BaTiO 3 ceramic were obtained, with dielectric constant of 1194.23 and loss of 0.0139 at room temperature and 1 kHz. Therefore, this work provides a robust strategy for suppressing the nanocrystal growth during sintering for MLCC applications. Graphical abstract Download : Download high-res image (263KB) Download : Download full-size image

Sintering and Microstructure of BaTiO3 Nano Particles Synthesized by Molten Salt Method

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

Room temperature synthesis of BaTiO3 nanoparticles using titanium bis(ammonium lactato) dihydroxide

Preparation of Nano BaTiO3-Based Dielectric Ceramics by Different Sintering Methods

Key to Enhance Thermoelectric Performance by Controlling Crystal Size of Strontium Titanate

Preparation of Nano-Structured BaTiO3 Thin Film by Electrophoretic Deposition and Its Characterization

Low-temperature synthesis of barium titanate thin films by nanoparticles electrophoretic deposition

Morphological Control of Ba-Ti-O Particles Prepared by Molten Salt Synthesis

Synthesis and Characterization of Ba(Zr0.15Ti0.85)O3 Nano Powders by Oxalate Precipitation Method

Synthesis of Micron‐Scale Platelet BaTiO3

Core-shell structure in nanocrystalline modified BaTiO3 dielectric ceramics prepared by different sintering methods

Ferroelectric properties and microwave sintering of BaTiO3 synthesized by using the alkoxide-hydroxide sol-gel process

Microstructural Characterization and Dielectric Properties of Single Crystalline BaTi2O5 Nanowires Prepared by Molten-Salt Method

Designing a glass nanoshell on barium titanium trioxide to suppress nanocrystal growth during sintering for fine-grain dielectric ceramics

Structure and Electrical Properties of BaTiO3 Prepared by Sol–gel Process

Synthesis of CaCu3Ti4O12 Micron-cubes and rods via high proportion molten salt method

Enhanced Sintering Characteristics And Microwave Dielectric Properties Of Li2tio3 Due To Nano-Size And Nonstoichiometry Effect

Synthesis, phase structure and dielectric properties of CoTiTa2O8 by molten salt method for LTCC application

Dielectric Properties of Fine-Grained BaTiO3 Prepared by Spark-Plasma-sintering

Microstructure Evolution and Dielectric Properties of Ultrafine Grained Batio3-Based Ceramics by Two-Step Sintering