Abstract:Sm0.2Ce0.8O1.9 (SDC)-impregnated La0.7Sr0.3MnO3 (LSM) composite cathodes were fabricated on anode-supported yttria-stabilized zirconia (YSZ) thin films. Electrochemical performances of the solid oxide fuel cells (SOFCs) were investigated in the present study. Four single cells, i.e., Cell-1, Cell-2, Cell-3 and Cell-4 were obtained after the fabrication of four different cathodes, i.e., pure LSM and SDC/LSM composites in the weight ratios of 25/75, 36/64 and 42/58, respectively. Impedance spectra under open-circuit conditions showed that the cathode performance was gradually improved with the increasing SDC loading. Similarly, the maximum power densities (MPD) of the four cells were increased with the SDC amount below 700°C. Whereas, the cell performance of Cell-4 was lower than that of Cell-3 at 800°C, arising from the increased concentration polarization at high current densities. This was caused by the lowered porosity with the impregnation cycle. This disadvantage could be suppressed by lowering the operating temperature or by increasing the oxygen concentration at the cathode side. The ratio of electrode polarization loss in the total voltage drop versus current density showed that the cell performance was primarily determined by the electrode polarization. The contribution of the ohmic resistance was increased when the operating temperature was lowered. When a 100mlmin−1 oxygen flow was introduced to the cathode side, Cell-3 produced MPDs of 1905, 1587 and 1179mWcm−2 at 800, 750 and 700°C, respectively. The high cell outputs demonstrated the merits of the novel and effective SDC-impregnated LSM cathodes.

Study on the Ohmic Resistance of Solid Oxide Fuel Cells Based on YSZ Membrane Fabricated by Slurry Spin Coating

A simple and easy one-step fabrication of thin BaZr0.1Ce0.7Y0.2O3−δ electrolyte membrane for solid oxide fuel cells

YSZ Thin Films Prepared by a Novel Powder Coating Process on Porous NiO-YSZ Cermet

Performance Evaluation of Thin Membranes Solid Oxide Fuel Cell Prepared by Pressure-Assisted Slurry-Casting

Study of Slurry Spin Coating Technique Parameters for the Fabrication of Anode-Supported YSZ Films for SOFCs

Study on YSZ film fuel cell by slurry spin coating method

Preparation of YSZ thin films for intermediate temperature solid oxide fuel cells by dip-coating method

Study on YSZ Membrane Electrolyte Fuel Cells Supported on Anode by Double-Layer Dry Pressing Method

Performance Evaluation of Solid Oxide Fuel Cells with Thin Film Electrolyte Fabricated by Binder‐Assisted Slurry Casting

Ni–Sm0.2Ce0.8O1.9 Anode-Supported YSZ Electrolyte Film and Its Application in Solid Oxide Fuel Cells

Fabrication and Performance Test of Solid Oxide Fuel Cells with Screen-Printed Yttria-Stabilized Zirconia Electrolyte Membranes

Sputter-deposited medium-temperature solid oxide fuel cells with multi-layer electrolytes

A Symmetrical Solid Oxide Fuel Cell Prepared by Dry-Pressing and Impregnating Methods

Anode-supported Solid Oxide Fuel Cell Based on Dense Electrolyte Membrane Fabricated by Filter-Coating

Fabrication of condense and thin YSZ electrolyte layer using novel thermal-assisted slurry spin coating method for IT-SOFC

Improvement of Cathode–electrolyte Interfaces of Tubular Solid Oxide Fuel Cells by Fabricating Dense YSZ Electrolyte Membranes with Indented Surfaces

Impedance analysis of thin YSZ electrolyte for low-temperature solid oxide fuel cells

Microstructure and Electrical Conductivity of Atmospheric Plasma-Sprayed LSM/YSZ Composite Cathode Materials

Effect of Sdc-Impregnated Lsm Cathodes on the Performance of Anode-Supported Ysz Films for Sofcs

Development of yttria-stabilized zirconia thin films via slurry spin coating for intermediate-to-low temperature solid oxide fuel cells

Preparation of Tubular YSZ Electrolyte and Its Application in Solid Oxide Fuel Cells