Abstract:To overcome significantly sluggish oxygen-ion conduction in the electrolytes of low-temperature solid-oxide fuel cells (SOFCs), numerous researchers have devoted considerable effort to fabricating the electrolytes as thin as possible. However, thickness is not the only factor that affects the electrolyte performance; roughness, grain size, and internal film stress also play a role. In this study, yttria-stabilized zirconia (YSZ) was deposited via a reactive sputtering process to fabricate high-performance thin-film electrolytes. Various sputtering chamber pressures (5, 10, and 15 mTorr) were investigated to improve the electrolytes. As a result, high surface area, large grain size, and residual tensile stress were successfully obtained by increasing the sputtering pressure. To clarify the correlation between the microstructure and electrolyte performance, a YSZ thin-film electrolyte was applied to anodized aluminum oxide-supported SOFCs composed of conventional electrode materials which are Ni and Pt as the anode and the cathode, respectively. The thin-film SOFC with YSZ deposited at 15 mTorr exhibited the lowest ohmic resistance and, consequently, the highest maximum power density (493 mW/cm2) at 500 °C whose performance is more than five times higher than that of the cell with YSZ deposited at 5 mTorr (94.1 mW/cm2). Despite the basic electrode materials, exceptionally high performance at low operating temperature was achieved via controlling the single fabrication condition for the electrolyte.

Nanocrystal Engineering of Thin-Film Yttria-Stabilized Zirconia Electrolytes for Low-Temperature Solid-Oxide Fuel Cells

A simple and easy one-step fabrication of thin BaZr0.1Ce0.7Y0.2O3−δ electrolyte membrane for solid oxide fuel cells

YSZ Thin Films Prepared by a Novel Powder Coating Process on Porous NiO-YSZ Cermet

Development of yttria-stabilized zirconia thin films via slurry spin coating for intermediate-to-low temperature solid oxide fuel cells

Efficient strategy to boost the electrochemical performance of yttrium stabilized zirconia electrolyte solid oxide fuel cell for low-temperature applications

High Performance Solid Oxide Fuel Cells Based on Tri-Layer Yttria-Stabilized Zirconia by Low Temperature Sintering Process

Fabrication of nanoscale yttria stabilized zirconia for solid oxide fuel cell

Impedance analysis of thin YSZ electrolyte for low-temperature solid oxide fuel cells

Scalable and facile fabrication of tri-layer electrolytes by reactive sputtering for efficient and durable solid oxide fuel cells

Efficiently enhance the proton conductivity of YSZ-based electrolyte for low temperature solid oxide fuel cell

Effect of Electrolyte Thickness of Thin Film Solid Oxide Fuel Cell on Nanostructure and Performance

Doped Zirconia/Ceria Electrolyte Fabricated at Low Temperature

Reactive Sputtered NiO-YSZ Anode Functional Layer for Thin Film Low-Temperature Solid Oxide Fuel Cell

One-step preparation of large-size 1.5-μm-thick robust YSZ electrolyte for high CH 4 conversion SOFCs at 600 °C

Fabrication, Microstructure and Properties of A Ysz Electrolyte for Sofcs

Preparation of Thin Electrolyte Film Via Dry Pressing/heating/ Quenching/calcining for Electrolyte-Supported SOFCs

Ionic Conductivity of Electrolytes Composed of Oleate-Capped Yttria-Stabilized Zirconia Nanoparticles

Fabrication and Characterizations of Ysz Electrolyte Films for Sofc

3D Printing of Robust 8YSZ Electrolytes with a Hyperfine Structure for Solid Oxide Fuel Cells

Sputter-deposited medium-temperature solid oxide fuel cells with multi-layer electrolytes

A new solid oxide fuel cell design based on thin film electrolytes