Abstract:The Nb and Co doped barium titanate was synthesized by sol-gel auto-ignition synthesis process (abbreviated SAS) and compared with the doped powder of the same composition prepared by conventional ball milling process. The phase structure, morphology of the two as-obtained powders and correlative dielectric properties of sintered BaTiO3-based ceramics were measured. The XRD analysis demonstrated that the SAS powder was the Ba(M0.047Ti0.953)O3(M=Nb, Co) solid solution based on BaTiO3; it further suggested that Nb and Co cations could replace the Ti ions and reach reciprocal balance of acceptors and donors during the decomposition step of the organic fuel by igniting the dried gel. TEM observation showed that the Ba(M0.047Ti0.953)O3(M=Nb, Co) particles were spherical with the size ranged from 30 to 110nm. Furthermore, it was found that the value of the Curie temperature of both the doped powders was being lowered in comparison with pure BaTiO3 (Tc≈128°C ); and the dielectric constant at room temperature of the SAS powder was 5840, which was much higher than that of the conventional ball milling doped powder(3013). It was attributed to the maximum homogeneous distribution of dopants in Ba-Ti initial solution at atomic level via the SAS process.

Preparation of nanocrystalline Ba3(Ca1.18Nb 1.82)O9-δ powder with sol-gel auto-ignition synthesis process

Low temperature preparation of nanocrystalline Sr0.5Ba 0.5Nb2O6 powders using an aqueous organic gel route

Synthesis and Characterization of BaCe<sub>0.8</sub>Y<sub>0.2</sub>O<sub>2.9</sub> Nanopowder by Sol-Gel Auto-Ignited Method

Synthesis and Characterization of BaCe0.8Y0.2O2.9 Nanopowder by Sol-Gel Auto-Ignited Method

An aqueous solution-gel method for low temperature synthesis of nanocrystalline NaNbO 3 and their ceramics

Process for Non-Agglomerated Nanometer-Sized Barium Titanate Powders by Sol-Gel Auto-Igniting Synthesis

NANO-SCALE Sm0.15Gd0.05Ce0.8O1.9POWDER PREPARED BY COUPLING ROUTES OF SOL-GEL AND LOW TEMPERATURE SELF-PROPAGATING COMBUSTION

LOW-TEMPERATURE PREPARATION OF NANO-CRYSTALLINE LITHIUM NIOBATE POWDERS BY THE POLYMERIC PRECURSOR METHOD

Preparation and Characterization of Nano-Crystalline Ba3Ti4Nb4O21 Microwave Dielectric Ceramic Powder

Low-temperature combustion synthesis of K0.5Na 0.5NbO3 powders

Gelation and heat treatment of preparing BaNc-4TisO-4 with îAutocombustion methods

Preparation and Characterization of Nanocrystalline (1−x)bisco3–xpbtio3 Powder

Preparation and Dielectric Properties of the Nb and Co Doped Barium Titanate by Sol-Gel Auto-Ignition Synthesis Process

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Synthesis and properties study of BaTi0.95Sc0.05O3-δ nanopowders and ceramics

Low-temperature combustion synthesis of nanometer tetragonal barium titanate powders

Preparation of Ba2Ti9O20 by gel self-propagation process

Low temperature preparation of strontium barium niobate powders from metal carboxylate gels

Preparation and Morphological Controlling of Nanophase Nanbo3 by Sol-Gel Method

Low-temperature Combustion Synthesis and Characterization of Nanosized Tetragonal Barium Titanate Powders