PVA-assisted Synthesis and Characterization of Nano-Crystalline La 3+ and Mg 2+ Co-Doped CeO 2 Electrolyte for Intermediate-Temperature Solid Oxide Fuel Cells
Chengcheng Wang,Linghong Luo,Yefan Wu,Yingchao Dong,Yonghong Chen,Jijun Shi,Liang Cheng,Bin Lin
DOI: https://doi.org/10.1007/s11581-012-0732-x
IF: 2.961
2012-01-01
Ionics
Abstract:A series of nano-crystalline ceria-based solid solution electrolyte, Ce0.8La0.2−x MgxO2−δ (x = 0.0, 0.05, 0.10, 0.15, and 0.2), were synthesized via the polyvinyl alcohol (PVA) assisted combustion method, and then characterized to the crystalline structure, powder morphology, sintering micro-structure, and electrical properties. Present study showed that Ce0.8La0.2−x Mg x O2−δ was exceedingly stable as a cubic phase in all temperature range and exhibited fine crystals ranging from 15 to 20 nm. After sintering at 1,400 °C, the as-prepared pellets exhibited a dense micro-structure with 96 % of theoretical density. The electrical conductivity was studied using AC impedance spectroscopy and it was observed that the composition Ce0.8La0.1 Mg0.1O2−δ showed higher electrical conductivity of 0.020 S cm−1 at 700 °C. The thermal expansion was measured using dilatometer technique in the temperature range 30–1,000 °C. The average thermal expansion coefficient of Ce0.8La0.1 Mg0.1O2−δ was 12.37 × 10−6 K−1, which was higher than that of the commonly used SOFC electrolyte YSZ (~10.8 × 10−6 K−1).