Abstract:Enhanced 395nm ultraviolet photoluminescence (PL) has been obtained from the SiO2/Ge SiO2/ SiO2 sandwiched structure. As light source for optical data storage system, this structure will be very useful in optoelectronic integration. Simultaneously, infrared light emission peaked at 780nm was also observed in this novel structure. In this paper, we discussed the origin of the infrared PL in terms of infrared spec- troscopy (FT-IR) and FL excitation (PLE) spectra. The constancy of the 780nm PL band with annealing temperature does suggest that it can not arise from both the quantum confinement on Ge, Si nanocrystals and the oxygen deficient defects of Ge and Si, because PL from these radiative centers all have peak shifts to some extent. The experimental results from FT-IR strongly suggest that the Ge-O-Ge vibration intensity and the 780nm PL intensity have a similar behavior with annealing temperature. So it is reasonable to be- lieve that the infrared PL band is very related to Ge oxides. Further PLE examination results indicate that it has the similar excitation process to the 395nm ultraviolet PL which comes from TⅡ'(T)→S0 optical transitions in GeO color centers, which has been confirmed by many research groups. So we believe that the 780nm PL should also originate from GeO color centers. The schematic diagram of electronic states of GeO molecule is presented to describe the carriers' excitation and recombination process in this kind of centers. The TⅡ'→S0 optical transitions in GeO color center is responsible for the infrared PL. In GeO molecules, all radiative transitions are intramolecular. Thus the PL bands from the GeO color centers are hardly influ- enced by the SiO2 network. That is why 780nm infrared PL has no wavelength change with different annealing temperature. Our work paves the way for the sandwiched structure's device applications.

Visible Photoluminescence Originated from Various Mechanisms During Step by Step Annealing

Origin of Infrared Photoluminescence from SiO_2/Ge: SiO_2/SiO_2 Sandwiched Structure [J]

Contribution of Multiple Emitting Centers to Luminescence from Si/SiO2 Multilayers with Step by Step Thermal Annealing

Influence of annealing on microstructures and photoluminescence of nano-composite silicon film

Intermediate Phase Silicon Structure Induced Enhancement of Photoluminescence from Thermal Annealed A-Si/Sio2 Multilayers

The Evolution Investigation Of Photoluminescence From A-Si : H/Sio2 To Nc-Si/Sio2 Multilayers

Pseudo Nanocrystal Silicon Induced Luminescence Enhancement in A-Si /sio 2 Multilayers

Light Emission from Si Nanoclusters Formed at Low Temperatures

Effect of annealing on microstructure and photoluminescence of nano-composite silicon film

Enhanced Green to Red Photoluminescence in Thermally Annealed of Amorphous-Si:H/sio2 Multilayers

Evolution of Photoluminescence from Si Nanocrystals Embedded in a SiO2 Matrix Prepared by Reactive Pulsed Laser Deposition

Pseudo nanocrystal silicon induced luminescence enhancement in a-Si /SiO2 multilayers

Visible Photo- and Electro-Luminescence from Laser-Crystallized A-Si:H and Its Based Multilayers

Correlation Between Luminescence and Structural Evolution of Si-rich Silicon Oxide Film Annealed at Different Temperatures

Strong ultraviolet and violet photoluminescence from Si-based anodic porous alumina films

The Evolution of Photoluminescence in Oxidized Amorphous Silicon Nitride Films by Rapid Thermal Annealing

Annealing-induced Blue Shift in Luminescence Band from Si-implanted SiO2 Layer

Photoluminescence Enhancement of Si Nanocrystals Embedded in SiO 2 by Thermal Annealing in Air

Visible and infrared photoluminescence from Er-doped SiOx

Luminescence from Si/SiO 2 with Si Implantation

Light Emission Properties and Mechanism of Low-Temperature Prepared Amorphous Sinx Films. I. Room-Temperature Band Tail States Photoluminescence