Synthesized Silicon-Substituted Hydroxyapatite Coating on Titanium Substrate by Electrochemical Deposition
Deng-Hu Li,Jun Lin,Dong-Yang Lin,Xiao-Xiang Wang
DOI: https://doi.org/10.1007/s10856-011-4310-y
2011-01-01
Journal of Materials Science Materials in Medicine
Abstract:Silicon-substituted hydroxyapaptite (Si-HA) coatings were prepared on titanium substrates by electrolytic deposition technique in electrolytes containing Ca2+, PO4 3− and SiO3 2− ions with various SiO3 2−/(PO4 3− + SiO3 2−) molar ratios(ηsi). The deposition was all conducted at a constant voltage of 3.0 V, with titanium substrate as cathode and platinum as anode, for 1 h at 85°C. The coatings thus prepared were characterized with inductively coupled plasma (ICP), X-ray diffraction (XRD), fourier transform infrared spectroscopy (FTIR), field-emission-type scanning electron microscope (FSEM). The results show that the silicon amount in the coatings increases linearly to about 0.48 wt% at first with increasing ηsi between 0 and 0.03, then increases slowly to about 0.55 wt% between 0.03 and 0.10 and finally maintains almost at a level around 0.55 wt% between 0.10 and 0.30. The tree-like Si-HA crystals are observed in the coatings prepared in the electrolyte of ηsi = 0.20. And the presence of silicon in electrolytes decreases the thickness of the coatings, with effect being more significant as ηsi increased. Additionally, the substitution of Si causes some OH− loss and changes the lattice parameters of hydroxyapatite (HA).