Abstract:To modify the coarse primary Mg2Si phase and improve mechanical properties of Mg2Si reinforced aluminum matrix composites, hypereutectic Al-18Mg(2)Si composites with different Eu contents were fabricated by per-manent mold casting and extrusion followed by heat treatment. Results show that the as-cast Al-18Mg(2)Si composites consisted of primary Mg2Si and eutectic structure (Al + Mg2Si). Eu addition can obviously modify the primary Mg2Si morphology from dendrite to flat truncated octahedron shape, and the average size also decreased from-90 mu m to-16 mu m with increasing Eu content from 0 to 0.1%. But further increasing Eu content would cause over-modification. After T6 treatment, sharp corners of primary Mg2Si were spheroidized and the average size of primary Mg2Si were further decreased. DTA result shows the nucleation temperature of primary Mg2Si increased by Eu addition. Al2Si2Eu phase can act as the heterogeneous nucleation substrate for the primary Mg2Si phase and thus refine the size of primary Mg2Si particle. TEM results show the segregation and/or selective adsorption of Eu on the {100} facets of primary Mg2Si suppress the growth of primary Mg2Si, and thus refine and modify the composites, which proposed to the dominant reason for the refinement and modification of the primary Mg2Si phase. Tensile tests show that the mechanical properties enhanced with increasing Eu content. The elongation and ultimate tensile strength of the T6-treated Al-18Mg(2)Si-0.1Eu composite improved to 5.2% and 241 MPa, which enhanced 225% and 91% compared to the unmodified as-cast Al-18%Mg2Si composite. It is concluded that the morphology transition of primary Mg2Si from dendrite to tetrakaidecahedron and the refinement of primary Mg2Si size with Eu modification, the passivation of the sharp corners in primary Mg2Si particles as well as the appearance of beta" precipitates all contribute to the improvement of the mechanical properties of the T6-treated Al-18Mg(2)Si composites.

Modification Performance of the Al-P Master Alloy for Eutectic and Hypereutectic Al-Si Alloys

In-situ Synthesis of Novel Al-P-O Master Alloy and Its Refinement and Modification Effects on Si Phases in Hypereutectic Al-30Si Alloys

The modification of electroless deposited Ni–P master alloy for hypereutectic Al–Si alloy

United Modification of Al-24Si Alloy by Al-P and Al-Ti-C Master Alloys

Microstructure control and performance evolution of hypereutectic Al–20Mg2Si alloy by novel Al–Ca–Sb master alloy

Mechanism of AlP Modifying the Morphology of Si in Al-20Si Alloys Based on Experimental Studies and First-Principles Calculations

Grain Refining Mechanism of Al-3B Master Alloy on Hypoeutectic Al-Si Alloys

Modification mechanism and tensile property of Al-9Si-0.4Mg-0.1Cu alloy

Evolution of Microstructure and Mechanical Properties of As-Cast Al-50si Alloy Due to Heat Treatment and P Modifier Content

Formation mechanism and conditions of fine primary silicon being uniformly distributed on single αAl matrix in Al-Si alloys

Effects of Si Content and the Addition Amount of Al-3b Master Alloy on the Solidification Structures of Hypoeutectic Al-Si Alloys

Effects of Refinement and Modification on Melt Structure of Hypoeutectic Al-Si Alloy

Analysis of Fe-, Cu-, Mg- and Sr-Based Phases in Al–Si Alloys: Role of P Addition

Factors affecting eutectic Si modification in Al-Si hypoeutectic alloy with the addition of Na, Sr, Eu and Yb

Grain refinement and eutectic modification of A356 casting alloy by adding Al-B-Sr master alloys and its effect on tensile properties

Effect of Sr Modification on the Microstructures, Mechanical Properties, and Thermal Conductivity of Hypoeutectic Al-13.6Cu-6Si Alloys

Effects of Eu modification and heat treatment on microstructure and mechanical properties of hypereutectic Al-Mg<sub>2</sub>Si composites

INFLUENCE OF ADDITIVE Sr OR Sb ON MODIFICATION OF Al-Si ALLOYS

Effect of Alloying Elements Mg and Cu on the Modification of Eutectic Silicon in Hypoeutectic Al-Si Alloys

The Circumstances and Development of Refinement and Modification of Hypoeutectic Al-Si Alloys

Development of Al–Nb–B master alloy with high Nb/B ratio for grain refinement of hypoeutectic Al–Si cast alloys