Abstract:The study demonstrates that applying an electric current during solidification significantly refines the primary Si phase. Moreover, adding phosphorus enhances this effect, particularly at 10 ppm, which is below the critical threshold of 20 ppm. The combined approach leads to improved nucleation and dispersion of aluminum phosphide, optimizing the microstructure for enhanced alloy performance. The efficient processing of hypereutectic Al–Si alloys depends on controlling the microstructure of the primary Si phase during solidification. This study investigates the effects of electric current and phosphorus (P) addition on the refinement of primary Si, with the results confirming that applying electric current during solidification refines the primary Si phase; introducing P further enhances this refinement. Notably, when 10 ppm of P is added (below the identified critical amount of 20 ppm), an improved refinement effect is observed compared with the application of either electric current or P alone. Applying an electric current generates a circulating flow within the melt, resulting in an increased cooling rate, which leads to improved nucleation behavior for the primary Si phase. In addition, the circulating flow generated within the melt influences the dispersion of aluminum phosphide during nucleation. Adding P at concentrations above 40 ppm does not yield further benefits, suggesting a saturation point for its efficacy. This study demonstrates that the concurrent electric current application and minimal P addition can significantly enhance the refinement of primary Si phases, offering a potent approach for optimizing the microstructural properties of hypereutectic Al–Si alloys.

The modification of electroless deposited Ni–P master alloy for hypereutectic Al–Si alloy

Modification Performance of the Al-P Master Alloy for Eutectic and Hypereutectic Al-Si Alloys

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

In-situ Synthesis of Novel Al-P-O Master Alloy and Its Refinement and Modification Effects on Si Phases in Hypereutectic Al-30Si Alloys

Mechanism of AlP Modifying the Morphology of Si in Al-20Si Alloys Based on Experimental Studies and First-Principles Calculations

Refinement of Primary Si Phase in Hypereutectic Al–Si Alloy by Electrically Assisted Solidification with P Addition

Microstructure control and performance evolution of hypereutectic Al–20Mg2Si alloy by novel Al–Ca–Sb master alloy

United Modification of Al-24Si Alloy by Al-P and Al-Ti-C Master Alloys

Formation mechanism and conditions of fine primary silicon being uniformly distributed on single αAl matrix in Al-Si alloys

Modification on Ni-P Amorphous Catalyst with Sio2 and Pd

Study on the Effect of Pre-Refinement and Heat Treatment on the Microstructure and Properties of Hypoeutectic Al-Si-Mg Alloy

Electrochemical Synthesis and Characterization of Ni–P Alloy Coatings from Eutectic–Based Ionic Liquid

The Circumstances and Development of Refinement and Modification of Hypoeutectic Al-Si Alloys

Fabrication of hypereutectic Al Si alloy with improved mechanical and thermal properties by hot extrusion

Behavior of phosphorus during solidification of the Si-Fe-P ternary alloy melt used in purification of MG-Si

Influence of Alloying Element Mg on Na and Sr Modifying Al-7Si Hypoeutectic Alloy

Evolution of Microstructure and Mechanical Properties of As-Cast Al-50si Alloy Due to Heat Treatment and P Modifier Content

Synergistic Effect of Lanthanum and Melt Purification on the Microstructure of Hypereutectic Al–Si Alloy

Improving Surface Electrochemical Polishing Quality of Additive Manufactured AlSi10Mg by Reconstituting the Si Phase

Electrodeposition of Ni-W-P alloy

Effects of Refinement and Modification on Melt Structure of Hypoeutectic Al-Si Alloy