Abstract:A supported Ni–P amorphous catalyst (Ni–P/SiO2) was prepared by electroless plating. When the sample was treated at elevated temperatures from 363 to 973 K in N2 flow for 2.0 h, the XRD patterns and SEM morphologies revealed that the Ni–P amorphous alloy crystallized stepwise from 673 to 873 K. The stabilizing effect of the support on the Ni–P amorphous alloy was observed by DSC, TPO, and TPR, which was attributed to the high dispersion of the Ni–P alloy particles in the support matrix, the affinity of SiO2 support for the Ni–P alloy particles, and the transfer of the heat produced during the crystallization from the surface to the bulk of the support. The change in the activity of the as-prepared Ni–P/SiO2 amorphous catalyst during heat treatment was measured using the liquid phase benzaldehyde hydrogenation as a probe and by comparing to that of the corresponding Ni/SiO2 crystalline catalyst. On one hand, the activity of both two catalysts decreased with the increase of the treating temperature owing to the decrease in surface active Ni atoms caused by the coalescence of small Ni particles at high temperature. On the other hand, the two catalysts exhibited considerably different catalytic behaviors during the heating treatment. (1) Only a smooth decrease in the activity of the Ni/SiO2 catalyst was observed with the increase of the treating temperature. While an impressive decrease in the activity of the Ni–P/SiO2 amorphous catalyst was observed in the temperature range from 673 to 873 K corresponding to its crystallization; (2) no significant change in the apparent activation energy (Ea) and the TOF value was observed during the heating pretreatment of the Ni/SiO2 catalyst. However, a considerable increase in Ea and a decrease in the TOF value were observed after the crystallization of the Ni–P/SiO2 amorphous catalyst. These results demonstrated a crystallization deactivation of the Ni–P/SiO2 amorphous catalyst. According to various characterizations, such as EXAFS, XRD, SEM, TEM, XPS, DSC, ICP, TPR, TPO, TPD, and hydrogen chemisorption, the decrease in the number of surface active Ni atoms and the surface P content in the Ni–P alloy, the change in the structural characteristics, and the adsorbing properties of the Ni active sites were the main factors responsible for the deactivation of Ni–P/SiO2 amorphous catalyst during the crystallization.

Modification on Ni-P Amorphous Catalyst with Sio2 and Pd

Effects of Active Metal Modification on C9 Petroleum Resin Hydrogention Activity of Pd/γ-Al2O3 Catalysts

Amorphous Alloy Deposited on Support and Its Hydrogenation Activity

The Crystallization Process and the Hydrogenation Activity of Ni-P/SiO2 Catalyst

Crystallization Deactivation of Ni–P/SiO2 Amorphous Catalystand the Stabilizing Effect of Silica Support on the Ni–P Amorphous Structure

Xps Studies On Surface Electronic Characteristics Of Ni-B And Ni-P Amorphous Alloy And Its Correlation To Their Catalytic Properties

Atomic intimacy in Pd 1 Ni/SiO 2 single-atom alloy prepared by galvanic replacement for enhanced semi-hydrogenation of acetylene

Preparations,Structures and Properties of Amorphous Ni-P Alloy Catalysts

Triethanolamine-mediated photodeposition formation of amorphous Ni-P alloy for improved H2-evolution activity of g-C3N4

Composition-Dependent Morphology of Bi- and Trimetallic Phosphides: Construction of Amorphous Pd-Cu-Ni-P Nanoparticles As a Selective and Versatile Catalyst.

Ultrasonic-assisted Synthesis of Pd–Ni Alloy Catalysts Supported on Multi-Walled Carbon Nanotubes for Formic Acid Electrooxidation

The effect of cyclic oxidation-reduction pretreatments on an amorphous Ni80P20 catalyst: an XPS/UPS/ISS study

Influence of Hydrothermal Modification on the Properties of Ni/Al2O3 Catalyst

Effect of TiO2 Support on the Composition, Morphology and Catalytic Property of the NiB Amorphous Alloy Catalyst

Au–Pd Alloying-Promoted Thermal Decomposition of PdO Supported on SiO2 and Its Effect on the Catalytic Performance in CO Oxidation

Depositing Pd on the Outmost Surface of Pd 1 Ni/SiO 2 Single-Atom Alloy via Atomic Layer Deposition for Selective Hydrogenation of Acetylene

Carbon-loaded Ultrafine Fully Crystalline Phase Palladium-Based Nanoalloy PdCoNi/C: Facile Synthesis and High Activity for Formic Acid Oxidation

Self-assembly of Mesoporous Ni–P Nanosphere Catalyst with Uniform Size and Enhanced Catalytic Activity in Nitrobenzene Hydrogenation

Ordered Mesoporous Ni Nanowires with Enhanced Hydrogenation Activity Prepared by Electroless Plating on Functionalized SBA-15

An amorphous nanoporous PdCuNi-S hybrid electrocatalyst for highly efficient hydrogen production

Pd–Ni ellipsoidal nano-alloys with excellent catalytic performance for oxygen reduction reaction