Effect of Vanadium/Boron Ratio on the Microstructure of Al-V-B Master Alloy and Their Grain Refining of Alloy A356.2
Yulan Zhou,Lihua Liu,Hailin Xue,Mengchao Ding,Gang Chen,Libing Liu,Jiangtao Zhao,Yunhu Zhang
DOI: https://doi.org/10.1007/s11837-024-06958-9
2024-11-08
JOM
Abstract:Al-V-B is a promising grain refiner for anti-silicon poisoning in casting aluminum-silicon alloys, yet its optimal composition with excellent refining capabilities is still ongoing. Therefore, it is important to further investigate the impact of the vanadium/boron (V/B) ratio on the efficacy of Al-V-B refiner. In this work, the effect of varying V/B ratios on the microstructure of Al-V-B master alloys prepared by the fluorine salt method and their grain refinement of A356.2 alloy was investigated. The results indicated that with the variation of V/B ratio, the average particle size in Al-V-B master alloy ranges from 1 μm to 1.8 μm. Furthermore, when the V/B ratio exceeds 1:2, the primary phases present in the Al-V-B master alloy are VB 2 and coarse Al 3 V. Conversely, when the V/B ratio is < 1:2, predominant phases in Al-V-B master alloy consist of small and uniformly distributed AlB 2 and VB 2 . In addition, the grain refinement effect of Al-V-B master alloy on A356.2 alloy is significantly enhanced when the V/B ratio is 1:2, the grain size of A356.2 alloy will increase.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy