Abstract:The inefficiency of grain refinement processes has traditionally been attributed to the limited utilization of heterogeneous nucleation particles within master alloy systems, resulting in the formation of abundant inactive particles. This study aims to investigate the alternative influences of particles by incorporating external micrometer-sized TiB2 particles into the grain refinement process. Through a series of experiments, the refinement efficiency, grain refinement mechanism, and resultant microstructure of TiB2 particle-induced grain refinement specimens are comprehensively examined using various microscopy and analytical techniques, including polarization microscopy (OM), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and transmission electron microscopy (TEM). Our findings demonstrate a direct correlation between increased levels of TiB2 particles and enhanced grain refinement efficiency. Moreover, the microstructure analysis reveals the distribution of TiB2 particles along grain boundaries, forming a coating due to self-assembly phenomena, while regions with a lower particle content may exhibit irregular grain structures. DSC analysis further confirms reduced undercooling, indicating the occurrence of heterogeneous nucleation events. However, TEM observations suggest that heterogeneous nucleation is not significantly influenced by the growth restriction factor attributed to TiAl3 2DC compounds. The grain refinement mechanism involving TiB2 particles is elucidated to entail both heterogeneous nucleation and physical growth restriction effects. Specifically, a reduction in average grain size is attributed not only to heterogeneous nucleation but also to the physical growth restriction effect facilitated by the TiB2 particle coating. This study offers insights into leveraging particles that do not participate in heterogeneous nucleation within master alloy-based grain refinement systems.

Grain Refinement of Al–Si–Cu Alloys by AlB2 and (Al,Ti)B2

Achieving superior grain refinement efficiency for Al–Si casting alloys through a novel Al–La–B grain refiner

Grain Refining Mechanism of Al-3B Master Alloy on Hypoeutectic Al-Si Alloys

The grain refinement of high-purity aluminum by aluminum-transition metal alloys

Quantities of grains of aluminum and those of TiB2 and Al3Ti particles added in the grain-refining processes

An experimental study of the effect of Ag, Cu, Li, Mg, Ni, Ti, Sc, Zr on grain refining in binary and multicomponent Al-based alloys

Heterogenous Grain Nucleation in Al-Si Alloys: Types of Nucleant Inoculation

Dual Grain Refinement Effect for Pure Aluminum with the Addition of Micrometer-Sized TiB2 Particles

Synergistic Effect of La and TiB2 Particles on Grain Refinement in Aluminum Alloy

Development of Mechanism of Grain Refinement in Aluminum

The Grain Refinement Mechanism of AlTiC, Al4B and Al3Ti4B Master Alloy in Pure Aluminium and Hypoeutectic Al-Si Alloys

Development of Al–Nb–B master alloy with high Nb/B ratio for grain refinement of hypoeutectic Al–Si cast alloys

The Grain Refinement of 1070 Alloy by Different Al-Ti-B Mater Alloys and Its Influence on the Electrical Conductivity

Novel Al-Ti-Nb-B grain refiners with superior efficiency for Al-Si alloys

Grain refinement and eutectic modification of A356 casting alloy by adding Al-B-Sr master alloys and its effect on tensile properties

Boosting the grain refinement of commercial Al alloys by compound addition of Sc

Effect of Vanadium/Boron Ratio on the Microstructure of Al-V-B Master Alloy and Their Grain Refining of Alloy A356.2

Performance Comparison of AlTiC and AlTiB Master Alloys in Grain Refinement of Commercial and High Purity Aluminum

Quantifying the effects of grain refiners (AlTiB and Y) on microstructure and properties in W319 alloys

Effect of trace boron on grain refinement of commercially pure aluminum by Al–5Ti–1B

Revealing the mechanism of grain refinement and anti Si-poisoning induced by (Nb, Ti)B2 with a sandwich-like structure