Abstract:PbTiO3 (PT) thin films were prepared by the sol-gel technique on Si(111) single crystal, fused quartz, and NaCl substrates using two precursor solutions: methanol and 2-methoxyethanol. Raman spectroscopy and x-ray diffraction were used to determine the effects of the precursor solution, substrate, annealing temperature, and film thickness on the film structure and crystallization behavior. The results indicate that the precursor solution plays an important role in the fabrication of pure perovskite PbTiO3 films. The films deposited from methanol solution are able to form the perovskite structure at lower crystallization temperature (similar to 430 degrees C). In contrast, the films deposited from 2-methoxyethanol solution easily form the pyrochlore phase. This is ascribed to the different mechanism of hydrolysis and condensation polymerization of the two precursor solutions. The Raman scattering results on various substrates have significant and interesting differences, especially for the films deposited from 2-methoxyethanol solution. In addition, with increasing the annealing temperature and film thickness, the full width of the Raman peaks at half-maximum decreases and the intensity increases. As to the position of the peaks, most Raman modes of PT films shift to lower frequencies due to the pressure effect in the films. (C) 1999 American Institute of Physics. [S0021-8979(99)04404-7].

Preparation and structure of preferentially oriented PbTiO3 glass-ceramic thin films by sol-gel process

Preparation of PZT Thick Film by a High Speed Sol-gel Method

Preparation of PbTiO3 thin films by a modified Sol-Gel processing

The oriented growth of PbTiO3 thin films deposited by a sol-gel process on substrates without lattice match

Preparation of PT Film Used as a Seed Layer to Fabricate Oriented PST Thin Films

Sol–gel derived nanocrystalline thin films of PbTiO3 on glass substrate

Preparation and Study of Oriented TiO2 Thin Film

Orientation Control in Sol–Gel‐Derived BiScO3–PbTiO3 Thin Films

Crystallization Behaviors and Electric Properties of (pb0.8ca0.2)tio3 Thin Films Prepared by a Sol–gel Route

Effects of Preparation Parameters on Microstructure and Properties of Calcium Titanate Oxides Thin Film

Highly Oriented Growth of PbTiO3 Ferroelectric Nanostructure Directed by Organic Molecules under Hydrothermal Condition

Effect of Tb3+ Doping on the Preferred Orientation of Lead Titanate Thin Film Prepared by Sol–gel Method on ITO/glass Substrates

Preferred orientation controlling of PZT (52–48) thin films prepared by sol–gel process

Preparation of High (100) Oriented PST Thin Films Deposited on PT/Tb Inducing Layer by Rf-Sputtering Method

Preparation and Optical Nonlinear Properties of PLT Ceramic Films by Sol-Gel Process

Low Temperature Preparation and Electric Properties of Highly (100)-Oriented Pb0.8 La0.1Ca0.1Ti0.975O3 Thin Films Prepared by a Sol–gel Route

Preparation on the [(Pb,La) (Zr,Ti)O3] ferroelectric thin films by using the Sol-Gel processing

Preparations and Dielectric Properties of Ba0.80Sr0.20TiO3/PbO–B2O3 Thick Films

Raman Spectroscopy And X-Ray Diffraction Study Of Pbtio3 Thin Films Prepared By Sol-Gel Technique

Crystallization, phase evolution and ferroelectric properties of sol-gel-synthesized Ba(Ti0.8Zr0.2)O3-x(Ba 0.7Ca0.3)TiO3 thin films

Preparation and microstructure analysis of Fe-doped PbTiO 3 ceramic