Abstract:Impact wear was carried out for annealed AISI1045 steel in this study. With the impact frequency of 600 times per min, an 8.29kN impact load was applied on the constant contact area of 540.08mm2 at the individual attack angles 60° and 90°. The microstructure of white layer for annealed AISI1045 steel was examined by SEM, TEM and HRTEM. It was found that nano structures with ferrite and cementite have been formed in white layer after impact of AISI1045 steel. Nano crystallization mechanism for ferrite is from moving, interacting and rearranging of dislocations, resulting in production of dislocation walls. With increasing strain, the density of pinned dislocations, whose Burgers vectors are usually vertical to the wall, correspondingly increases along the dislocation wall, i.e., θ/b increases. That, finally, forms subgrain boundaries with small angle θ. In addition, the density of slippery or shear-susceptible dislocations, whose Burgers vectors are often parallel to dislocation walls, also increases at the same time. The slipping of dislocations in many places along the boundary of subgrains will result in the rotation of crystals to form boundaries with large angles. Nano crystallized mechanism for cementite is mainly due to shearing fracture, neck-like shrinkage fracture and carbides dissolving under the impact. The cementite thinning and the formation of slipping stages will increase the surface energy per volume, which causes the dissolution of cementite. The chemical potential energy difference between carbon atoms and cementite is a driver for dissolving cementite. The moving, reacting and proliferating of dislocations promote carbon atoms diffusing and migrating to distant ferrite from the boundary of cementite, which accelerates the dissolution of cementite.

Delamination mechanism of white layer under high stress impact wear

The Failure Models Induced by White Layers During Impact Wear

Wear behavior of carbon steels under high-stress impact

Microstructures of surface white layer and internal white adiabatic shear band

High stress impact wear resistance of high silicon bainitic steel

Wear Mechanism of Nano-Structured Surface Layer under High Impact Energy

A Study On The Behavior Of Adiabatic Shear Bands In Impact Wear

Formation Mechanism and Influence of White Etching Area on Contact Fatigue Spalling of M50 Bearing Steel

Effect of Si on Wear Resistance of Bainitic Cast Steel under High Stress Impact

Nano Structure and Transformation Mechanism of White Layer for Aisi1045 Steel During Impact Wear

Damage evolution around white etching layer during uniaxial loading

Microstructure Transformation in the Worn Surface Layer of Austenite-Bainite Steel with Nodular Eutectics during Impact Wear

Formation Mechanisms and Crack Propagation Behaviors of White Etching Layers and Brown Etching Layers on Raceways of Failure Bearings

Impact wear mechanism of 2Cr13 steel under small stress multi-impact conditions

Hybrid structure of white layer in high carbon steel – Formation mechanism and its properties

Study on the Microstructure of White Layer during Precision Hard Part Machining

The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel

White etching area damage induced by shear localization in rolling contact fatigue of bearing steel

Subsurface Microstructure Evolution of Hadfield Steel under High Impact Energy

Analysis on the Cracking of Thin Hard Films Considering the Effects of Interfacial Delamination

The effect of hydrogen on the impact-abrasion wear behavior in nanostructured bainitic steels