Abstract:Carbide-free nano-bainite steel holds significant potential for applications in mining as an ultra-high strength wear-resistant steel, but the wear mechanisms are not yet fully understood. This study aims to explore the effect of austempering temperature on microstructure, mechanical properties and wear resistance of carbide-free nano-bainitic steel. The relationship between the content and mechanical stability of retained austenite (RA) and mechanical properties was investigated to elucidate the mechanisms of pin-on-disc wear and impact wear. The results show that in the range of M s ∼300 °C, the phase transformation incubation period and completion time significantly increase with decreasing austempering temperature, which is mainly related to higher phase transformation driving force resulting from a larger subcooling degree and slow growth of carbon content in RA. Optimal strength and hardness of 2099 MPa and 615 HBW, respectively, are achieved after austempering at 210 °C for 83 h. Austempering at 270 °C for 11 h yields the best balance of strength and plasticity, with a strength-plasticity product of 28.8 GPa%. The micro-cutting mechanism of pin-on-disc wear leads to serious weight loss. The RA with poor mechanical stability accelerates the stress-induced martensite transformation, while internal stress support due to volume expansion reduces the penetration depth of abrasive particles. The weight loss in impact wear is primarily caused by shedding due to fatigue failure. With the increase of RA content and mechanical stability, the persistent stress-induced martensite transformation effectively hinders micro-crack propagation, thereby enhancing impact wear resistance.

High stress impact wear resistance of high silicon bainitic steel

Effect of Si on Wear Resistance of Bainitic Cast Steel under High Stress Impact

Wear behavior of carbon steels under high-stress impact

Effects of TiC and residual austenite synergistic strengthening mechanism on impact-abrasive wear behavior of bainite steel

The Microstructure Transformations and Wear Properties of Nanostructured Bainite Steel with Different Si Content

Delamination mechanism of white layer under high stress impact wear

Influence of Toughness and Retained Austenite on Wear Behaviour of Carbide-Free Bainite in High Silicon Steel

Influence of Re-Ti Modification on the High Impact Wear Resistance of High Si Bainitic Cast Steel

Comparison of wear performance of bainitic and martensitic structure with similar fracture toughness and hardness at different wear conditions

The effect of hydrogen on the impact-abrasion wear behavior in nanostructured bainitic steels

Bainite transformation under the effect of large stress in a carbide-free bainite steel

Effect of Surface Impacting Parameters on Wear Resistance of High Manganese Steel

New insight into the dry rolling-sliding wear mechanism of carbide-free bainitic and pearlitic steel

Effect of impact on wear resistance of high chromium cast iron and austenitic stainless steel

Microstructure and Mechanical Properties of Chromium-Alloyed Silicon Cast Steel

Effect of Silicon on Precipitates of High-Silicon Austenitic Stainless Steel

Current Development of Carbide Free Bainitic and Retained Austenite on Wear Resistance in High Silicon Steel

Effect of Austempering Temperature on Microstructure Evolution, Mechanical Properties and Wear Resistance of Carbon-free Nano-bainite Steel

Carbon Atom Distribution and Impact Toughness of High-Carbon Bainitic Steel

Two-Step Isothermal Bainitic Transformation in Medium-Carbon Low-Si Steels with Exceptional Mechanical Properties and Wear Resistance

Mechanisms of Strengthening and Toughening of Austempered High Silicon Cast Steel