Study on the Microstructure of White Layer during Precision Hard Part Machining

Sujiang Dai,Tong Xing,Donghui Wen,Julong Yuan,Yong Dai

DOI: https://doi.org/10.3321/j.issn:1004-132X.2006.10.005

2006-01-01

Abstract:This paper investigated the microstructure of white layers formed during machining process of GCr15 hardened steel at large flank wear land(0.1 mm). A hard turned surface with white layer usually consists of three layers: a white layer (untempered martensite), a transition layer (over-tempered martensite), and the bulk material. The martensite, austenite and carbide are observed in the white layer generated by the high temperature during hard turning, the hardness of white layer is larger than that of bulk material, and the hardness of transition layer is lower. High hardness of a turned white layer is caused by extremely small grain size and high dislocation density. The depth of white layer is about 10~15 μm with the flank wear which reached 0.1 mm, the optimal width of the flank wear which generated low depth of white layer is essential to ensure the superfinishing process. The severe plastic deformation is the main mechanism of white layer formation during precision hard part machining process.