Effects of matrix cracks on delamination of composite laminates subjected to low-velocity impact

Tian Ouyang,Wei Sun,Rui Bao,Riming Tan

DOI: https://doi.org/10.1016/j.compstruct.2020.113354

IF: 6.3

2021-04-01

Composite Structures

Abstract:This paper investigates delamination mechanisms of composite laminates subjected to low-velocity impact. To obtain delamination data between plies with different fiber orientations, thermal-deply tests were conducted on quasi-isotropic laminates after low-velocity impact. Regularities of delamination positions in different interfaces as well as the matrix cracks distribution through the laminate thickness were analyzed. It is found that delamination positions are influenced by matrix cracks and the distribution of matrix cracks is determined by the out-of-plane shear stress distribution. To illustrate the formation process of delamination, a novel micro-block finite element model was established. It is revealed that due to the interaction between adjacent cracks, inter-laminar cracks growing towards each other show higher stress intensity factors and are thus more likely to form delamination. This crack propagation pattern eventually leads to the formation of two centrosymmetric fan-shaped delaminations in each interface.

mechanics,materials science, composites

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the mechanism of delamination in composite laminates under low - velocity impact. Specifically, the research focuses on how matrix cracks affect the location and morphology of delamination and the relationship between these cracks and delamination. Through experiments and numerical simulations, the authors aim to reveal the distribution law of matrix cracks in composite laminates after low - velocity impact and their influence on delamination formation.

The main contributions of the paper are as follows:
1. **Experimental observation**: The delamination locations at different interfaces and the distribution of matrix cracks were analyzed through pyrolytic layer testing.
2. **Numerical modeling**: A new micro - block finite - element model was established to simulate the formation processes of matrix cracks and delamination.
3. **Mechanism explanation**: It was explained how matrix cracks are formed under low - velocity impact and how they affect the formation of delamination, especially the formation of two centrosymmetric fan - shaped delamination regions.

Through these studies, the authors hope to more accurately predict and understand the damage behavior of composite laminates under low - velocity impact, thereby providing theoretical support for design and application.