Abstract:Numerous studies have demonstrated that under low-velocity, low-energy impact conditions, although the surface damage to fiber-reinforced composite laminates may be minimal, significant internal damage can occur. Consequently, a progressive damage finite element model was specifically developed for thermoplastic carbon fiber-reinforced composite laminates subjected to low-speed impact loads, with the objective of analyzing the damage behavior of laminates under impacts of varying energy levels. The model utilizes a three-dimensional Hashin criterion for predicting intralayer damage initiation, with cohesive elements based on bilinear traction-separation law for predicting interlaminar delamination initiation, and incorporates a damage constitutive model based on equivalent displacement to characterize fiber damage evolution, along with the B-K criterion for interlaminar damage evolution. The impact response of laminates at energy levels of 5 J, 10 J, 15 J, 20 J, and 25 J was analyzed through numerical simulation, drop-hammer experiments, and XCT non-destructive testing. The results indicated that the simulation outcomes closely correspond with the experimental findings, with both the predicted peak error and absorbed energy error maintained within a 5% margin, and the trends of the mechanical response curves aligning closely with the experimental data. The damage patterns predicted by the numerical simulations were consistent with the results obtained from XCT scans. The study additionally revealed that the impact damage of the laminates primarily stems from interlaminar delamination and intralayer tensile failure. Initial damage typically presents as internal delamination; hence, enhancing interlaminar bonding performance can significantly augment the overall load-bearing capacity of the laminate.

Study on the delamination behavior of thick composite laminates under low-energy impact

Delamination prediction in composite laminates under low-velocity impact

Investigation on the Compressive Mechanical Properties of Ultra-Thick CFRP Laminates

Applicability Evaluation of Damage Evolution Models in Simulating Repeated Low-Velocity Impact Behavior of Composite Laminates

Experimental and Simulation Study on Failure of Thermoplastic Carbon Fiber Composite Laminates under Low-Velocity Impact

A delamination criterion for laminated composites under low-velocity impact

Delamination Analysis of Carbon Fiber/Epoxy Composite Laminates under Different Loading Rates Using Acoustic Emission

Numerical Prediction of Compressive Residual Strengths of a Quasi-Isotropic Laminate with Low-Velocity Impact Delamination

Review of delamination predictive methods for low speed impact of composite laminates

Research on low‐velocity impact resistance of carbon fiber composite laminates

Experimental and numerical investigations on the dynamic response of woven carbon fiber reinforced thick composite laminates under low-velocity impact

Simulation Analysis of Delamination Damage for the Thick-Walled Composite-Overwrapped Pressure Vessels

Effects of matrix cracks on delamination of composite laminates subjected to low-velocity impact

Low velocity impact and compression after impact of thin and thick laminated carbon fiber composite panels

Application of a delamination model to laminated composite structures

Predictive modeling for hat-stiffener delamination during low velocity impact

Failures of laminates under nonpenetrative impacts

Finite element analysis on impact response and damage mechanism of composite laminates under single and repeated low-velocity impact

On the Distribution of Delamination in Composite Structures and Compressive Strength Prediction for Laminates with Embedded Delaminations

Low‐velocity multiple impact damage characteristics and numerical simulation of carbon fiber/epoxy composite laminates

DELAMINATED COMPOSITE LAMINATES' RESPONSE UNDER LOW-VELOCITY IMPACT