Abstract:This work investigates the heterogeneous deformation and failure of HR3C austenitic stainless steel welded joints at room and typical service temperatures. Such types of welded joints are widely used in the new generation of fossil fuel power stations and are known to suffer from premature high temperature failure. Observation of in-service failures revealed that cracks may nucleate either in the heat affected zone or in the weld metal. The main objective of this work is to identify the local microstructural conditions and stress–strain fields responsible for both ductile failure and micro-crack nucleation within the weldment at low and high temperatures, respectively. To that purpose, a novel multi-scale micromechanics-based modelling framework is proposed. It relies on representative weld microstructure models digitally reconstructed from EBSD measurements, and dislocation density-based crystal plasticity models to describe the behaviour of individual grains in each weld region. A novel thermo-dynamically consistent relation for the configuration stored energy per unit volume is derived from the crystal plasticity framework. The single crystal models are calibrated and validated from a combination of uniaxial tensile tests on cross-weld specimens using high resolution digital image correlation techniques, representative volume elements of the polycrystals at the macro-scale, as well as micropillar compression tests at the scale of the individual grains. Predictions of heterogeneous inelastic deformation fields within the weldment at both 22 °C and 665 °C, and of micropillar compression behaviour of the individual weld single crystal phases are consistent with experimental data. The experimentally observed ductile failure of the weld metal at room temperature is successfully predicted using a Gurson-type void nucleation, growth and coalescence constitutive model. The suitability of the stored strain energy density and the accumulated plastic strain as crack initiation/creep failure indicators is investigated. It was found that predicted creep lifetimes with either indicator were very similar, and that they were relatively accurate for low stress levels.

Towards a general damage law for interior micro-defect induced fatigue cracking in martensitic steels

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

DAMAGE ACCUMULATION, FRACTURE AND POST FRACTURE ANALYSES FOR INITIALLY FLAWED STEEL STRUCTURES

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Towards Fully Automatic Modelling of the Fracture Process in Quasi-Brittle and Ductile Materials: a Unified Crack Growth Criterion

In-situ observation of strain evolution and ratchetting of growing fatigue cracks

Prediction of Low Cycle Fatigue Crack Growth under Mixed-mode Loading Conditions Using Cohesive Zone Models

Micro-mechanics investigation of heterogeneous deformation fields and crack initiation driven by the local stored energy density in austenitic stainless steel welded joints

A fatigue life prediction approach to interior cracking induced high cycle and very high cycle fatigue for surface‐carburized steels

Computational Monitoring of an Initial Fatigue Crack Incubation and Growth in a Smooth Specimen

Investigation of low cycle fatigue crack propagation behavior of 316H steel at 550°C based on cyclic response and damage accumulation: experiment and modelling

Micro-crack Damage in Strip of Fracture Process Zone

Surface Vs. Interior Failure Behaviors in a Structural Steel under Gigacycle Fatigue: Failure Analysis and Life Prediction

Micro-Defect Effect on Gigacycle Fatigue S-N Property and Very Slow Crack Growth of High Strength Low Alloy Steel

The mechanism of internal fatigue-crack initiation and early growth in a titanium alloy with lamellar and equiaxed microstructure

Crystal plasticity modeling of grain boundary softening and fatigue in U75V pearlite steel under low strain conditions: A study of cyclic rolling contact fatigue

Micromechanical Modeling of Strain-Softening in Microcrack-Weakened Quasi-Brittle Materials

Experimental and Numerical Investigation of Ductile Fracture of Carbon Steel Structural Components

A fatigue life prediction approach for porosity defect-induced failures in directed energy deposited Ti-6Al-4V considering crack growth environment

Dynamic Localized Shear Failure Influenced by Changing Rates in Brittle Solids Containing Initial Microcracks